Low Temperature Sintering of BaO-R2O3-TiO2 Microwave Ceramics
碩士 === 國立臺北科技大學 === 材料及資源工程系碩士班 === 91 === Sintered BaO-(La1-xNdx)2O3-4TiO2 at 1450℃ show microwave dielectric properties : εr=99, Q×f=5120GHz.However, excellent microwave dielectric properties cannot fit the requirements The objective of present work is to evaluate the glass compositions...
Main Authors: | , |
---|---|
Other Authors: | |
Format: | Others |
Language: | zh-TW |
Published: |
2003
|
Online Access: | http://ndltd.ncl.edu.tw/handle/46949973997817285193 |
id |
ndltd-TW-091TIT00681009 |
---|---|
record_format |
oai_dc |
spelling |
ndltd-TW-091TIT006810092015-10-13T13:35:32Z http://ndltd.ncl.edu.tw/handle/46949973997817285193 Low Temperature Sintering of BaO-R2O3-TiO2 Microwave Ceramics BaO-R2O3-TiO2微波介電陶瓷之低溫燒結研究 Chun-Yu Su 蘇純玉 碩士 國立臺北科技大學 材料及資源工程系碩士班 91 Sintered BaO-(La1-xNdx)2O3-4TiO2 at 1450℃ show microwave dielectric properties : εr=99, Q×f=5120GHz.However, excellent microwave dielectric properties cannot fit the requirements The objective of present work is to evaluate the glass compositions to decrease sintering temperature without influence dielectric properties. The results exhibited that Li2CO3-B2O3-SiO2 and B2O3-SiO2-ZnO were suitable additives for BaO-(La1-xNdx)2O3-4TiO2.Moreover the dielectric conatant is enhanced by the increasing relative density, and decreased by increasing the amount of glasses ,so as the Q×f values. Based on dense bulks with 10 wt% Li2CO3-B2O3-SiO2 glasses addition, the densification temperature is 1150℃ under the good microwave dielectric properties: εr>84, Q×f>3000.Furthermore 10wt% B2O3-SiO2-ZnO(+1wt%Na2O、K2O) added BaO-(La1-xNdx)2O3-4TiO2 can be sintered to achieve theoretical densities of 90% at 1050℃, and giveεr >70, Q×f>3500. As the consequence, the sintering temperature of the BaO-(La1-xNdx)2O3-4TiO2 can be effectively lowered with glasses addition and keep the good dielectric properties for LTCC materials applied to multilayer microwave devices. Yuh-Ruey Wang Sea-Fue Wang 王玉瑞 王錫福 2003 學位論文 ; thesis 99 zh-TW |
collection |
NDLTD |
language |
zh-TW |
format |
Others
|
sources |
NDLTD |
description |
碩士 === 國立臺北科技大學 === 材料及資源工程系碩士班 === 91 === Sintered BaO-(La1-xNdx)2O3-4TiO2 at 1450℃ show microwave dielectric properties : εr=99, Q×f=5120GHz.However, excellent microwave dielectric properties cannot fit the requirements
The objective of present work is to evaluate the glass compositions to decrease sintering temperature without influence dielectric properties. The results exhibited that Li2CO3-B2O3-SiO2 and B2O3-SiO2-ZnO were suitable additives for BaO-(La1-xNdx)2O3-4TiO2.Moreover the dielectric conatant is enhanced by the increasing relative density, and decreased by increasing the amount of glasses ,so as the Q×f values. Based on dense bulks with 10 wt% Li2CO3-B2O3-SiO2 glasses addition, the densification temperature is 1150℃ under the good microwave dielectric properties:
εr>84, Q×f>3000.Furthermore 10wt% B2O3-SiO2-ZnO(+1wt%Na2O、K2O) added BaO-(La1-xNdx)2O3-4TiO2 can be sintered to achieve theoretical densities of 90% at 1050℃, and giveεr >70, Q×f>3500.
As the consequence, the sintering temperature of the BaO-(La1-xNdx)2O3-4TiO2 can be effectively lowered with glasses addition and keep the good dielectric properties for LTCC materials applied to multilayer microwave devices.
|
author2 |
Yuh-Ruey Wang |
author_facet |
Yuh-Ruey Wang Chun-Yu Su 蘇純玉 |
author |
Chun-Yu Su 蘇純玉 |
spellingShingle |
Chun-Yu Su 蘇純玉 Low Temperature Sintering of BaO-R2O3-TiO2 Microwave Ceramics |
author_sort |
Chun-Yu Su |
title |
Low Temperature Sintering of BaO-R2O3-TiO2 Microwave Ceramics |
title_short |
Low Temperature Sintering of BaO-R2O3-TiO2 Microwave Ceramics |
title_full |
Low Temperature Sintering of BaO-R2O3-TiO2 Microwave Ceramics |
title_fullStr |
Low Temperature Sintering of BaO-R2O3-TiO2 Microwave Ceramics |
title_full_unstemmed |
Low Temperature Sintering of BaO-R2O3-TiO2 Microwave Ceramics |
title_sort |
low temperature sintering of bao-r2o3-tio2 microwave ceramics |
publishDate |
2003 |
url |
http://ndltd.ncl.edu.tw/handle/46949973997817285193 |
work_keys_str_mv |
AT chunyusu lowtemperaturesinteringofbaor2o3tio2microwaveceramics AT sūchúnyù lowtemperaturesinteringofbaor2o3tio2microwaveceramics AT chunyusu baor2o3tio2wēibōjièdiàntáocízhīdīwēnshāojiéyánjiū AT sūchúnyù baor2o3tio2wēibōjièdiàntáocízhīdīwēnshāojiéyánjiū |
_version_ |
1717738342506823680 |