Investigation on the Physical Properties of LCP( Zenite)/PC Blends
碩士 === 長庚大學 === 化工與材料工程研究所 === 93 === The aim of this study was to investigate the physical properties of liquid crystalline polymer (LCP, Zenite)/polycarbonate (PC) blends. The blends were prepared through an internal mixer (Haake Polydrive). Under the blending condition, the possible reaction betw...
Main Authors: | , |
---|---|
Other Authors: | |
Format: | Others |
Language: | zh-TW |
Published: |
2005
|
Online Access: | http://ndltd.ncl.edu.tw/handle/86555050846264296561 |
id |
ndltd-TW-093CGU00063010 |
---|---|
record_format |
oai_dc |
spelling |
ndltd-TW-093CGU000630102015-10-13T15:29:16Z http://ndltd.ncl.edu.tw/handle/86555050846264296561 Investigation on the Physical Properties of LCP( Zenite)/PC Blends 液晶高分子(LCP)/無定形聚碳酸酯(PC)摻合體物理性質研究 Hsu.Sheng-Kai 許勝凱 碩士 長庚大學 化工與材料工程研究所 93 The aim of this study was to investigate the physical properties of liquid crystalline polymer (LCP, Zenite)/polycarbonate (PC) blends. The blends were prepared through an internal mixer (Haake Polydrive). Under the blending condition, the possible reaction between the components did not occur. The differential scanning calorimetry (DSC) results confirmed that the LCP/PC blend system was partial miscible. The scanning electron microscope (SEM) photographs showed that epoxy-4221 played a compatibilizer role for the partial miscible LCP/PC blend system. The dynamic mechanical properties results showed that LCP/PC(75/25) blend exhibited the best storage modulus among all the samples. Cone and plate viscometer results showed that viscosity of the samples decreased as the PC content increased and the addition of epoxy-4221 as well. Fang-Chyou Chiu 邱方遒 2005 學位論文 ; thesis 146 zh-TW |
collection |
NDLTD |
language |
zh-TW |
format |
Others
|
sources |
NDLTD |
description |
碩士 === 長庚大學 === 化工與材料工程研究所 === 93 === The aim of this study was to investigate the physical properties of liquid crystalline polymer (LCP, Zenite)/polycarbonate (PC) blends. The blends were prepared through an internal mixer (Haake Polydrive). Under the blending condition, the possible reaction between the components did not occur. The differential scanning calorimetry (DSC) results confirmed that the LCP/PC blend system was partial miscible. The scanning electron microscope (SEM) photographs showed that epoxy-4221 played a compatibilizer role for the partial miscible LCP/PC blend system. The dynamic mechanical properties results showed that LCP/PC(75/25) blend exhibited the best storage modulus among all the samples. Cone and plate viscometer results showed that viscosity of the samples decreased as the PC content increased and the addition of epoxy-4221 as well.
|
author2 |
Fang-Chyou Chiu |
author_facet |
Fang-Chyou Chiu Hsu.Sheng-Kai 許勝凱 |
author |
Hsu.Sheng-Kai 許勝凱 |
spellingShingle |
Hsu.Sheng-Kai 許勝凱 Investigation on the Physical Properties of LCP( Zenite)/PC Blends |
author_sort |
Hsu.Sheng-Kai |
title |
Investigation on the Physical Properties of LCP( Zenite)/PC Blends |
title_short |
Investigation on the Physical Properties of LCP( Zenite)/PC Blends |
title_full |
Investigation on the Physical Properties of LCP( Zenite)/PC Blends |
title_fullStr |
Investigation on the Physical Properties of LCP( Zenite)/PC Blends |
title_full_unstemmed |
Investigation on the Physical Properties of LCP( Zenite)/PC Blends |
title_sort |
investigation on the physical properties of lcp( zenite)/pc blends |
publishDate |
2005 |
url |
http://ndltd.ncl.edu.tw/handle/86555050846264296561 |
work_keys_str_mv |
AT hsushengkai investigationonthephysicalpropertiesoflcpzenitepcblends AT xǔshèngkǎi investigationonthephysicalpropertiesoflcpzenitepcblends AT hsushengkai yèjīnggāofēnzilcpwúdìngxíngjùtànsuānzhǐpccànhétǐwùlǐxìngzhìyánjiū AT xǔshèngkǎi yèjīnggāofēnzilcpwúdìngxíngjùtànsuānzhǐpccànhétǐwùlǐxìngzhìyánjiū |
_version_ |
1717764932601118720 |