Nano-polyaniline Synthesis and Characterization
碩士 === 國立臺北科技大學 === 有機高分子研究所 === 93 === The polyaniline nanopolymers were synthesized in this research . The polymerization temperature are 5℃ and 25℃,and DBSA was used to be surfactants and dopants. The particle size was measured by particle size distribution analysis. The physical properties was i...
| Main Authors: | , |
|---|---|
| Other Authors: | |
| Format: | Others |
| Language: | zh-TW |
| Published: |
2005
|
| Online Access: | http://ndltd.ncl.edu.tw/handle/j4w663 |
| Summary: | 碩士 === 國立臺北科技大學 === 有機高分子研究所 === 93 === The polyaniline nanopolymers were synthesized in this research . The polymerization
temperature are 5℃ and 25℃,and DBSA was used to be surfactants and dopants. The particle size was measured by particle size distribution analysis. The physical properties was investigated by DSC,SEM,and FT-IR.
On the other hand, the carbon nanotube and polyacrylic acid were mixed with polyaniline to increase the electrical conductivity. It was found that the conductivity was increase significantly by mixing these two components.
|
|---|