氧化鈷觸媒應用於乙醇蒸氣重組反應之研究
碩士 === 國防大學中正理工學院 === 應用化學研究所 === 95 === A high valence cobalt oxide, CoOx has been prepared by the precipitation- oxidation method. Further, the nanosize cobalt was refined by controlling calcination temperature. The modified CoOx with lanthanum, La/CoOx(5, 10, 20 wt %) was prepared by impregnation...
Main Authors: | , |
---|---|
Other Authors: | |
Format: | Others |
Language: | zh-TW |
Published: |
2007
|
Online Access: | http://ndltd.ncl.edu.tw/handle/50061968718802102720 |
id |
ndltd-TW-095CCIT0500009 |
---|---|
record_format |
oai_dc |
spelling |
ndltd-TW-095CCIT05000092016-05-25T04:14:20Z http://ndltd.ncl.edu.tw/handle/50061968718802102720 氧化鈷觸媒應用於乙醇蒸氣重組反應之研究 Lee Chia-Chan 李嘉展 碩士 國防大學中正理工學院 應用化學研究所 95 A high valence cobalt oxide, CoOx has been prepared by the precipitation- oxidation method. Further, the nanosize cobalt was refined by controlling calcination temperature. The modified CoOx with lanthanum, La/CoOx(5, 10, 20 wt %) was prepared by impregnation method. The particle sizes and structures of catalysts were physically characterized by X-ray diffraction (XRD) and transmission electron microscopy (TEM). The technique of temperature programmed reduction (TPR) was used to explore the reductive behavior of the oxidized catalysts and inspected the interaction between lanthanum oxide and cobalt oxide. Evaluation of catalytic activities on steam reforming of ethanol(SRE) over cobalt catalysts were proceeded in a fixed-bed reactor. In order to find the optimal conditions of SRE and understand the mechanism of SRE over CoOx and La/CoOx catalysts. Based on the XRD and TPR analysis, we found that both the phase compositions and the reduction temperatures(Tred) of species were affected with the calcination temperature(Tc). The higher Tc, increased the particle size and raised the Tred. Lanthanum modified cobalt catalysts could enhance the thermal stability and shift the Tred to high temperature. In SRE test, the CoOx possessed the best performance among the series of CoOx catalysts under TR = 375℃ and H2O/EtOH = 4, the yield of hydrogen(YH2 )approached 5.7 the selectivity of CO(SCO ) approached 1.6 %. The lifetime over CoOx catalyst only maintained 48 hr. Whereas, the lifetime of 10La/CoOx(H) catalyst exceeded 60 hr under TR = 425℃ and H2O/EtOH = 4, the yield of hydrogen(YH2 = 5.9 ) was competed with the theoretical value. 汪成斌 葉君棣 2007 學位論文 ; thesis 95 zh-TW |
collection |
NDLTD |
language |
zh-TW |
format |
Others
|
sources |
NDLTD |
description |
碩士 === 國防大學中正理工學院 === 應用化學研究所 === 95 === A high valence cobalt oxide, CoOx has been prepared by the precipitation- oxidation method. Further, the nanosize cobalt was refined by controlling calcination temperature. The modified CoOx with lanthanum, La/CoOx(5, 10, 20 wt %) was prepared by impregnation method. The particle sizes and structures of catalysts were physically characterized by X-ray diffraction (XRD) and transmission electron microscopy (TEM). The technique of temperature programmed reduction (TPR) was used to explore the reductive behavior of the oxidized catalysts and inspected the interaction between lanthanum oxide and cobalt oxide. Evaluation of catalytic activities on steam reforming of ethanol(SRE) over cobalt catalysts were proceeded in a fixed-bed reactor. In order to find the optimal conditions of SRE and understand the mechanism of SRE over CoOx and La/CoOx catalysts.
Based on the XRD and TPR analysis, we found that both the phase compositions and the reduction temperatures(Tred) of species were affected with the calcination temperature(Tc). The higher Tc, increased the particle size and raised the Tred. Lanthanum modified cobalt catalysts could enhance the thermal stability and shift the Tred to high temperature. In SRE test, the CoOx possessed the best performance among the series of CoOx catalysts under TR = 375℃ and H2O/EtOH = 4, the yield of hydrogen(YH2 )approached 5.7 the selectivity of CO(SCO ) approached 1.6 %. The lifetime over CoOx catalyst only maintained 48 hr. Whereas, the lifetime of 10La/CoOx(H) catalyst exceeded 60 hr under TR = 425℃ and H2O/EtOH = 4, the yield of hydrogen(YH2 = 5.9 ) was competed with the theoretical value.
|
author2 |
汪成斌 |
author_facet |
汪成斌 Lee Chia-Chan 李嘉展 |
author |
Lee Chia-Chan 李嘉展 |
spellingShingle |
Lee Chia-Chan 李嘉展 氧化鈷觸媒應用於乙醇蒸氣重組反應之研究 |
author_sort |
Lee Chia-Chan |
title |
氧化鈷觸媒應用於乙醇蒸氣重組反應之研究 |
title_short |
氧化鈷觸媒應用於乙醇蒸氣重組反應之研究 |
title_full |
氧化鈷觸媒應用於乙醇蒸氣重組反應之研究 |
title_fullStr |
氧化鈷觸媒應用於乙醇蒸氣重組反應之研究 |
title_full_unstemmed |
氧化鈷觸媒應用於乙醇蒸氣重組反應之研究 |
title_sort |
氧化鈷觸媒應用於乙醇蒸氣重組反應之研究 |
publishDate |
2007 |
url |
http://ndltd.ncl.edu.tw/handle/50061968718802102720 |
work_keys_str_mv |
AT leechiachan yǎnghuàgǔchùméiyīngyòngyúyǐchúnzhēngqìzhòngzǔfǎnyīngzhīyánjiū AT lǐjiāzhǎn yǎnghuàgǔchùméiyīngyòngyúyǐchúnzhēngqìzhòngzǔfǎnyīngzhīyánjiū |
_version_ |
1718280453167775744 |