| Summary: | 碩士 === 國立中山大學 === 材料科學研究所 === 95 === In recent years, series of high-entropy alloy have been well developed with high hardness and high temperature stability. These properties could apply in hard surface welding technology.
The previous research showed that Al0.5CoCrCuFeNi based alloy contained excellent abrasive and adhesive wear resistant properties. According to the results of first year project, the post heat treatment is required for Type A (Al0.3CrFe1.5MnNi0.5 ) and B (Al0.5CrFe1.5MnNi0.5) alloys. It is not suitable for the industrial field service in certain repairing application. This research project will modify the Al0.5CrFe1.5MnNi0.5 base high-entropy alloy in the alloy content of Cr and Ni. These new alloy called Type D high entropy alloys include BCC and FCC two phases. We expect BCC part will provide the wear hardness and FCC part could improve the ductility during the wearing stage. The FCC phase may improve the manufacture of welding rods, also.
The research contents include, (1) Type D high entropy alloys weld rod evaluation, (2) wear test, (3) microstructure analysis using electron micro-probe
|
|---|