High Frequency Fe-Y-B Magnetic Thin Films
碩士 === 國立清華大學 === 材料科學工程學系 === 95 === The purpose of this thesis was to develop magnetic thin films for high frequency applications. We made of Fe-Y-B bulk metallic glasses that had developed in our laboratory. The study was divided into three parts: First, the Fe-Y-B ternary system. Second, the Fe-...
Main Authors: | , |
---|---|
Other Authors: | |
Format: | Others |
Language: | zh-TW |
Published: |
2007
|
Online Access: | http://ndltd.ncl.edu.tw/handle/11927783099800037035 |
id |
ndltd-TW-095NTHU5159063 |
---|---|
record_format |
oai_dc |
spelling |
ndltd-TW-095NTHU51590632015-10-13T16:51:14Z http://ndltd.ncl.edu.tw/handle/11927783099800037035 High Frequency Fe-Y-B Magnetic Thin Films 高頻鐵釔硼磁性薄膜材料的研究與開發 Hui-Wen Liu 劉惠雯 碩士 國立清華大學 材料科學工程學系 95 The purpose of this thesis was to develop magnetic thin films for high frequency applications. We made of Fe-Y-B bulk metallic glasses that had developed in our laboratory. The study was divided into three parts: First, the Fe-Y-B ternary system. Second, the Fe-Y-B films which were annealed under a magnetic field after sputtering. Third, Fe-Y-B-M quaternary system. Electrical, magnetic and high frequency properties of these films were evaluated. Amorphous Fe-Y-B thin films were sputter-deposited using composite target with Y chip on a Fe80B20 target with area ratio of Y 5.6 %. The films obtained at a dc power of 40 W showed a resistivity ρ ~ 860 μΩ-cm, 4πMs ~ 1.01 T and Hc ~ 27 Oe. The film was also shown to have a high resonance frequency fr ~ 2.1 GHz. No magnetic uniaxial anisotropy was found in the as-deposited films. The thin films obtained at a dc power of 80 W showed a resistivity ρ ~ 340 μΩ-cm, 4πMs ~ 0.86 T and a low Hc ~ 1.5 Oe. The film also had a fr ~ 1.0 GHz and a very high μ’ above 700 which remain nearly constant up to ~ 0.75 GHz. The thin films obtained at a dc power of 60 W with Y chip on a Fe80B20 target with area ratio of Y 9 % were taken to anneal under 2500 G. Nano-grained α-Fe appealed after field annealing at 300 oC for 30 min. All films demonstrated a minor crystalline growth and good thermal stability up to 500oC for 30 min. Above 300 oC, a small increase occurred in crystallite size from 5 nm up to 6.7 nm at 500 oC. The film after 450 oC field-annealing for 30 min showed good high frequency property with Ms ~ 1.07 T, Hc ~ 66.3 Oe and fr > 3 GHz. The corresponding values were Ms ~ 1.08 T, Hc ~ 47 Oe, fr ~ 2.7 GHz for film after 400 oC field-annealing for 2 hr. The appearance of nano-grained α-Fe after field-annealing is showed beneficial to promote the high frequency properties. The quaternary films showed inferior properties. In summary the Fe-Y-B films showed high resistivity and high frequency properties, which are promising for high frequency applications. T.S. Chin 金重勳 2007 學位論文 ; thesis 88 zh-TW |
collection |
NDLTD |
language |
zh-TW |
format |
Others
|
sources |
NDLTD |
description |
碩士 === 國立清華大學 === 材料科學工程學系 === 95 === The purpose of this thesis was to develop magnetic thin films for high frequency applications. We made of Fe-Y-B bulk metallic glasses that had developed in our laboratory. The study was divided into three parts: First, the Fe-Y-B ternary system. Second, the Fe-Y-B films which were annealed under a magnetic field after sputtering. Third, Fe-Y-B-M quaternary system. Electrical, magnetic and high frequency properties of these films were evaluated.
Amorphous Fe-Y-B thin films were sputter-deposited using composite target with Y chip on a Fe80B20 target with area ratio of Y 5.6 %. The films obtained at a dc power of 40 W showed a resistivity ρ ~ 860 μΩ-cm, 4πMs ~ 1.01 T and Hc ~ 27 Oe. The film was also shown to have a high resonance frequency fr ~ 2.1 GHz. No magnetic uniaxial anisotropy was found in the as-deposited films. The thin films obtained at a dc power of 80 W showed a resistivity ρ ~ 340 μΩ-cm, 4πMs ~ 0.86 T and a low Hc ~ 1.5 Oe. The film also had a fr ~ 1.0 GHz and a very high μ’ above 700 which remain nearly constant up to ~ 0.75 GHz.
The thin films obtained at a dc power of 60 W with Y chip on a Fe80B20 target with area ratio of Y 9 % were taken to anneal under 2500 G. Nano-grained α-Fe appealed after field annealing at 300 oC for 30 min. All films demonstrated a minor crystalline growth and good thermal stability up to 500oC for 30 min. Above 300 oC, a small increase occurred in crystallite size from 5 nm up to 6.7 nm at 500 oC. The film after 450 oC field-annealing for 30 min showed good high frequency property with Ms ~ 1.07 T, Hc ~ 66.3 Oe and fr > 3 GHz. The corresponding values were Ms ~ 1.08 T, Hc ~ 47 Oe, fr ~ 2.7 GHz for film after 400 oC field-annealing for 2 hr. The appearance of nano-grained α-Fe after field-annealing is showed beneficial to promote the high frequency properties.
The quaternary films showed inferior properties. In summary the Fe-Y-B films showed high resistivity and high frequency properties, which are promising for high frequency applications.
|
author2 |
T.S. Chin |
author_facet |
T.S. Chin Hui-Wen Liu 劉惠雯 |
author |
Hui-Wen Liu 劉惠雯 |
spellingShingle |
Hui-Wen Liu 劉惠雯 High Frequency Fe-Y-B Magnetic Thin Films |
author_sort |
Hui-Wen Liu |
title |
High Frequency Fe-Y-B Magnetic Thin Films |
title_short |
High Frequency Fe-Y-B Magnetic Thin Films |
title_full |
High Frequency Fe-Y-B Magnetic Thin Films |
title_fullStr |
High Frequency Fe-Y-B Magnetic Thin Films |
title_full_unstemmed |
High Frequency Fe-Y-B Magnetic Thin Films |
title_sort |
high frequency fe-y-b magnetic thin films |
publishDate |
2007 |
url |
http://ndltd.ncl.edu.tw/handle/11927783099800037035 |
work_keys_str_mv |
AT huiwenliu highfrequencyfeybmagneticthinfilms AT liúhuìwén highfrequencyfeybmagneticthinfilms AT huiwenliu gāopíntiěyǐpéngcíxìngbáomócáiliàodeyánjiūyǔkāifā AT liúhuìwén gāopíntiěyǐpéngcíxìngbáomócáiliàodeyánjiūyǔkāifā |
_version_ |
1717775301776244736 |