The influence of heat treatment strength on Cr-Mo steel -A case study of bicycle spindle
碩士 === 國立中興大學 === 機械工程學系所 === 96 === Heat treatment process is often used to improve mechanical properties of components. Various heat treatment processes have different influences on material. This paper is to show the influences of strength on Cr-Mo Steel between austempering and quenching-temperi...
Main Authors: | , |
---|---|
Other Authors: | |
Format: | Others |
Language: | zh-TW |
Published: |
2008
|
Online Access: | http://ndltd.ncl.edu.tw/handle/06961999969993070417 |
id |
ndltd-TW-096NCHU5311055 |
---|---|
record_format |
oai_dc |
spelling |
ndltd-TW-096NCHU53110552016-05-09T04:13:47Z http://ndltd.ncl.edu.tw/handle/06961999969993070417 The influence of heat treatment strength on Cr-Mo steel -A case study of bicycle spindle 熱處理對鉻鉬鋼強度之影響-以自行車BB軸心為例 Huang-Chi Chen 陳皇吉 碩士 國立中興大學 機械工程學系所 96 Heat treatment process is often used to improve mechanical properties of components. Various heat treatment processes have different influences on material. This paper is to show the influences of strength on Cr-Mo Steel between austempering and quenching-tempering heat treatment processes, with the use of bicycle spindles as the experimental subject. During the experiment austempering process involves 860℃ austenizing temperature.360℃ austempering. And 60-minute austempering time condition. An average maximum load of 6363.67kg was achieved, resulting 65901.33kg-mm total torque. Other hand, quenching- tempering heat treatment process involves 880℃ quenching temperature, tempering at 530℃, for 20-minute tempering criteria. Maximum load, in average, was 4605kg, resulting 50559.67kg-mm total torque. After comparing the experiment data gathered between Austempering and quenching- tempering processes, we discover that austempering results 1758.67kg increase in maximum load. The increase was about 38.2%. Results 15341.66kg-mm increase in total torque. The increase was about 30.34% Therefore, a Cr-Mo Steel bicycle spindle with austempering heat treatment can have better strength in terms of maximum load and total torque. During the experiment minimum deformation involves 760℃ austenizing temperature.200℃ austempering. And 3.85mm thickness of spindle condition. An average minimum deformation of 1.08mm was achieved, the increase was 0.81mm than before heat treatment. Pai-Chung Tseng 曽柏昌 2008 學位論文 ; thesis 56 zh-TW |
collection |
NDLTD |
language |
zh-TW |
format |
Others
|
sources |
NDLTD |
description |
碩士 === 國立中興大學 === 機械工程學系所 === 96 === Heat treatment process is often used to improve mechanical properties of components. Various heat treatment processes have different influences on material. This paper is to show the influences of strength on Cr-Mo Steel between austempering and quenching-tempering heat treatment processes, with the use of bicycle spindles as the experimental subject.
During the experiment austempering process involves 860℃ austenizing temperature.360℃ austempering. And 60-minute austempering time condition. An average maximum load of 6363.67kg was achieved, resulting 65901.33kg-mm total torque. Other hand, quenching- tempering heat treatment process involves 880℃ quenching temperature, tempering at 530℃, for 20-minute tempering criteria. Maximum load, in average, was 4605kg, resulting 50559.67kg-mm total torque.
After comparing the experiment data gathered between Austempering and quenching- tempering processes, we discover that austempering results 1758.67kg increase in maximum load. The increase was about 38.2%. Results 15341.66kg-mm increase in total torque. The increase was about 30.34% Therefore, a Cr-Mo Steel bicycle spindle with austempering heat treatment can have better strength in terms of maximum load and total torque.
During the experiment minimum deformation involves 760℃ austenizing temperature.200℃ austempering. And 3.85mm thickness of spindle condition. An average minimum deformation of 1.08mm was achieved, the increase was 0.81mm than before heat treatment.
|
author2 |
Pai-Chung Tseng |
author_facet |
Pai-Chung Tseng Huang-Chi Chen 陳皇吉 |
author |
Huang-Chi Chen 陳皇吉 |
spellingShingle |
Huang-Chi Chen 陳皇吉 The influence of heat treatment strength on Cr-Mo steel -A case study of bicycle spindle |
author_sort |
Huang-Chi Chen |
title |
The influence of heat treatment strength on Cr-Mo steel -A case study of bicycle spindle |
title_short |
The influence of heat treatment strength on Cr-Mo steel -A case study of bicycle spindle |
title_full |
The influence of heat treatment strength on Cr-Mo steel -A case study of bicycle spindle |
title_fullStr |
The influence of heat treatment strength on Cr-Mo steel -A case study of bicycle spindle |
title_full_unstemmed |
The influence of heat treatment strength on Cr-Mo steel -A case study of bicycle spindle |
title_sort |
influence of heat treatment strength on cr-mo steel -a case study of bicycle spindle |
publishDate |
2008 |
url |
http://ndltd.ncl.edu.tw/handle/06961999969993070417 |
work_keys_str_mv |
AT huangchichen theinfluenceofheattreatmentstrengthoncrmosteelacasestudyofbicyclespindle AT chénhuángjí theinfluenceofheattreatmentstrengthoncrmosteelacasestudyofbicyclespindle AT huangchichen rèchùlǐduìluòmùgāngqiángdùzhīyǐngxiǎngyǐzìxíngchēbbzhóuxīnwèilì AT chénhuángjí rèchùlǐduìluòmùgāngqiángdùzhīyǐngxiǎngyǐzìxíngchēbbzhóuxīnwèilì AT huangchichen influenceofheattreatmentstrengthoncrmosteelacasestudyofbicyclespindle AT chénhuángjí influenceofheattreatmentstrengthoncrmosteelacasestudyofbicyclespindle |
_version_ |
1718262801520132096 |