A study on the Corrosion Behaviors of NiAlFe Intermetallic Alloys
碩士 === 中國文化大學 === 材料科學與奈米科技研究所 === 96 === The thesis studied the electrochemical property on the NiAlFe based intermetallic alloys, including Ni47.5Al25Fe27.5, (Ni47.5Al25Fe27.5) 99Cr1,(Ni47.5Al25Fe27.5)99Nb1. For testing the corrosion rates of these three alloys,these alloys were statically immerse...
Main Authors: | , |
---|---|
Other Authors: | |
Format: | Others |
Language: | zh-TW |
Published: |
2008
|
Online Access: | http://ndltd.ncl.edu.tw/handle/99975522104273293054 |
id |
ndltd-TW-096PCCU0159029 |
---|---|
record_format |
oai_dc |
spelling |
ndltd-TW-096PCCU01590292017-04-07T04:33:29Z http://ndltd.ncl.edu.tw/handle/99975522104273293054 A study on the Corrosion Behaviors of NiAlFe Intermetallic Alloys NiAlFe基介金屬合金之腐蝕特性研究 Ting-Nung,Chen 陳定穠 碩士 中國文化大學 材料科學與奈米科技研究所 96 The thesis studied the electrochemical property on the NiAlFe based intermetallic alloys, including Ni47.5Al25Fe27.5, (Ni47.5Al25Fe27.5) 99Cr1,(Ni47.5Al25Fe27.5)99Nb1. For testing the corrosion rates of these three alloys,these alloys were statically immersed in 50 % of commercial nitric acid,hydrochloric acid and sulfuric acid, respectively. The results were alsocompared with the corrosion rates of commercial 304 stainless steel. In addition, the polarization curves of these three alloys in sodium chloride solutions with different concentrations were also tested for measuring their corrosion potentials and corrosion currents. The results indicated that the corrosion resistances of these alloys immersed in hydrochloric acid and sulfuric acid were better than that of commercial 304 stainless steel. However, the corrosion resistances of these alloys immersed in nitric acid were worse than that of commercial 304 stainless steel. Adding Cr or Nb into Ni47.5Al25Fe27.5 alloy could not improve their corrosion resistances of hydrochloric acid or sulfuric acid;but it could improve the corrosion resistance of nitric acid ofNi47.5Al25Fe27.5 alloy. During the tests of polarization curves in sodium chloride solutions, increasing the chloride ion would result in reducing the passivity phenomenon for (Ni47.5Al25Fe27.5) 99Cr1, (Ni47.5Al25Fe27.5) 99Nb1 alloys.Also, the passive films of the alloys would be destroyed quickly when the concentration of sodium chloride solutions were increased. Therefore, the current densities of the anodic polarization curves thus decreased. Chun-Huei,Tsau 曹春暉 2008 學位論文 ; thesis 73 zh-TW |
collection |
NDLTD |
language |
zh-TW |
format |
Others
|
sources |
NDLTD |
description |
碩士 === 中國文化大學 === 材料科學與奈米科技研究所 === 96 === The thesis studied the electrochemical property on the NiAlFe based
intermetallic alloys, including Ni47.5Al25Fe27.5, (Ni47.5Al25Fe27.5) 99Cr1,(Ni47.5Al25Fe27.5)99Nb1. For testing the corrosion rates of these three alloys,these alloys were statically immersed in 50 % of commercial nitric acid,hydrochloric acid and sulfuric acid, respectively. The results were alsocompared with the corrosion rates of commercial 304 stainless steel. In addition, the polarization curves of these three alloys in sodium chloride solutions with different concentrations were also tested for measuring their corrosion potentials and corrosion currents.
The results indicated that the corrosion resistances of these alloys
immersed in hydrochloric acid and sulfuric acid were better than that of commercial 304 stainless steel. However, the corrosion resistances of these alloys immersed in nitric acid were worse than that of commercial 304 stainless steel. Adding Cr or Nb into Ni47.5Al25Fe27.5 alloy could not improve their corrosion resistances of hydrochloric acid or sulfuric acid;but it could improve the corrosion resistance of nitric acid ofNi47.5Al25Fe27.5 alloy.
During the tests of polarization curves in sodium chloride solutions,
increasing the chloride ion would result in reducing the passivity
phenomenon for (Ni47.5Al25Fe27.5) 99Cr1, (Ni47.5Al25Fe27.5) 99Nb1 alloys.Also, the passive films of the alloys would be destroyed quickly when the concentration of sodium chloride solutions were increased. Therefore, the current densities of the anodic polarization curves thus decreased.
|
author2 |
Chun-Huei,Tsau |
author_facet |
Chun-Huei,Tsau Ting-Nung,Chen 陳定穠 |
author |
Ting-Nung,Chen 陳定穠 |
spellingShingle |
Ting-Nung,Chen 陳定穠 A study on the Corrosion Behaviors of NiAlFe Intermetallic Alloys |
author_sort |
Ting-Nung,Chen |
title |
A study on the Corrosion Behaviors of NiAlFe Intermetallic Alloys |
title_short |
A study on the Corrosion Behaviors of NiAlFe Intermetallic Alloys |
title_full |
A study on the Corrosion Behaviors of NiAlFe Intermetallic Alloys |
title_fullStr |
A study on the Corrosion Behaviors of NiAlFe Intermetallic Alloys |
title_full_unstemmed |
A study on the Corrosion Behaviors of NiAlFe Intermetallic Alloys |
title_sort |
study on the corrosion behaviors of nialfe intermetallic alloys |
publishDate |
2008 |
url |
http://ndltd.ncl.edu.tw/handle/99975522104273293054 |
work_keys_str_mv |
AT tingnungchen astudyonthecorrosionbehaviorsofnialfeintermetallicalloys AT chéndìngnóng astudyonthecorrosionbehaviorsofnialfeintermetallicalloys AT tingnungchen nialfejījièjīnshǔhéjīnzhīfǔshítèxìngyánjiū AT chéndìngnóng nialfejījièjīnshǔhéjīnzhīfǔshítèxìngyánjiū AT tingnungchen studyonthecorrosionbehaviorsofnialfeintermetallicalloys AT chéndìngnóng studyonthecorrosionbehaviorsofnialfeintermetallicalloys |
_version_ |
1718436213867675648 |