Electrocatalytic Activities of Pt/C and PtRu/C Prepared Using Colloidal Precursor Technique.
碩士 === 國立臺灣大學 === 化學工程學研究所 === 97 === Platinum and platinum-ruthenium alloy catalysts on carbon were prepared by colloidal precursor technique. The adsorption of CO and its effect on the hydrogen oxidation reaction on the catalyst were investigated by cyclic voltammetry (CV) and the rotating disk el...
Main Authors: | , |
---|---|
Other Authors: | |
Format: | Others |
Language: | zh-TW |
Published: |
2009
|
Online Access: | http://ndltd.ncl.edu.tw/handle/23155219270342272507 |
id |
ndltd-TW-097NTU05063044 |
---|---|
record_format |
oai_dc |
spelling |
ndltd-TW-097NTU050630442016-05-04T04:31:48Z http://ndltd.ncl.edu.tw/handle/23155219270342272507 Electrocatalytic Activities of Pt/C and PtRu/C Prepared Using Colloidal Precursor Technique. 以膠體先驅物法製備之Pt/C和PtRu/C陽極觸媒電催化活性之研究 Pei-Wen Ho 何佩紋 碩士 國立臺灣大學 化學工程學研究所 97 Platinum and platinum-ruthenium alloy catalysts on carbon were prepared by colloidal precursor technique. The adsorption of CO and its effect on the hydrogen oxidation reaction on the catalyst were investigated by cyclic voltammetry (CV) and the rotating disk electrode (RDE) techniques. PtCl2, RuCl3 and N(oct4)[ Bet3H] were used to prepared the catalysts. The particle sizes of Pt and PtRu for 5.4~27.2 wt% Pt/C and 6.5~26.6 wt% PtRu/C prepared, determined by X-ray diffraction and transmission electron microscope, were in the range of 3.1~8.9 nm and 2.6~3.3 nm, respectively, which are slightly larger than those of commercial catalysts. By reducing the electro-active surface area of the catalyst through the adsorption of CO, the current density in the catalyst layer and thus the exchange current density for hydrogen oxidation reaction on the catalyst can be measured using the rotating disk electrode (RDE) method. The exchange current densities of Pt/C and PtRu/C in 0.5M H2SO4 at 28℃ were determined to be 5mAcm-2 and 1.4mAcm-2, respectively. Pt/C had higher electrocatalytic activity for hydrogen oxidation than PtRu/C, but Pt/C was poisioned by CO faster than PtRu/C. The results of this research may contribute to the development of CO-tolerant platinum-based alloy anode catalysts for low-temperature fuel cells. 施信民 2009 學位論文 ; thesis 133 zh-TW |
collection |
NDLTD |
language |
zh-TW |
format |
Others
|
sources |
NDLTD |
description |
碩士 === 國立臺灣大學 === 化學工程學研究所 === 97 === Platinum and platinum-ruthenium alloy catalysts on carbon were prepared by colloidal precursor technique. The adsorption of CO and its effect on the hydrogen oxidation reaction on the catalyst were investigated by cyclic voltammetry (CV) and the rotating disk electrode (RDE) techniques. PtCl2, RuCl3 and N(oct4)[ Bet3H] were used to prepared the catalysts. The particle sizes of Pt and PtRu for 5.4~27.2 wt% Pt/C and 6.5~26.6 wt% PtRu/C prepared, determined by X-ray diffraction and transmission electron microscope, were in the range of 3.1~8.9 nm and 2.6~3.3 nm, respectively, which are slightly larger than those of commercial catalysts.
By reducing the electro-active surface area of the catalyst through the adsorption of CO, the current density in the catalyst layer and thus the exchange current density for hydrogen oxidation reaction on the catalyst can be measured using the rotating disk electrode (RDE) method. The exchange current densities of Pt/C and PtRu/C in 0.5M H2SO4 at 28℃ were determined to be 5mAcm-2 and 1.4mAcm-2, respectively. Pt/C had higher electrocatalytic activity for hydrogen oxidation than PtRu/C, but Pt/C was poisioned by CO faster than PtRu/C.
The results of this research may contribute to the development of CO-tolerant platinum-based alloy anode catalysts for low-temperature fuel cells.
|
author2 |
施信民 |
author_facet |
施信民 Pei-Wen Ho 何佩紋 |
author |
Pei-Wen Ho 何佩紋 |
spellingShingle |
Pei-Wen Ho 何佩紋 Electrocatalytic Activities of Pt/C and PtRu/C Prepared Using Colloidal Precursor Technique. |
author_sort |
Pei-Wen Ho |
title |
Electrocatalytic Activities of Pt/C and PtRu/C Prepared Using Colloidal Precursor Technique. |
title_short |
Electrocatalytic Activities of Pt/C and PtRu/C Prepared Using Colloidal Precursor Technique. |
title_full |
Electrocatalytic Activities of Pt/C and PtRu/C Prepared Using Colloidal Precursor Technique. |
title_fullStr |
Electrocatalytic Activities of Pt/C and PtRu/C Prepared Using Colloidal Precursor Technique. |
title_full_unstemmed |
Electrocatalytic Activities of Pt/C and PtRu/C Prepared Using Colloidal Precursor Technique. |
title_sort |
electrocatalytic activities of pt/c and ptru/c prepared using colloidal precursor technique. |
publishDate |
2009 |
url |
http://ndltd.ncl.edu.tw/handle/23155219270342272507 |
work_keys_str_mv |
AT peiwenho electrocatalyticactivitiesofptcandptrucpreparedusingcolloidalprecursortechnique AT hépèiwén electrocatalyticactivitiesofptcandptrucpreparedusingcolloidalprecursortechnique AT peiwenho yǐjiāotǐxiānqūwùfǎzhìbèizhīptchéptrucyángjíchùméidiàncuīhuàhuóxìngzhīyánjiū AT hépèiwén yǐjiāotǐxiānqūwùfǎzhìbèizhīptchéptrucyángjíchùméidiàncuīhuàhuóxìngzhīyánjiū |
_version_ |
1718259762928287744 |