焚化飛灰燒製成輕質骨材及其工程性質之研究
碩士 === 正修科技大學 === 營建工程研究所 === 98 === Abstract This study is to make use of the treated incineration fly ash, mudstone powder, glass cullet which is combined with swell and flux etc. after made into lightweight granular aggregate of different sizes through the processes of mixing and rotating granula...
Main Authors: | , |
---|---|
Other Authors: | |
Format: | Others |
Language: | zh-TW |
Published: |
2010
|
Online Access: | http://ndltd.ncl.edu.tw/handle/79154414244238351502 |
id |
ndltd-TW-098CSU00582024 |
---|---|
record_format |
oai_dc |
spelling |
ndltd-TW-098CSU005820242015-10-28T04:07:10Z http://ndltd.ncl.edu.tw/handle/79154414244238351502 焚化飛灰燒製成輕質骨材及其工程性質之研究 Huang, Qun-xiang 黃群翔 碩士 正修科技大學 營建工程研究所 98 Abstract This study is to make use of the treated incineration fly ash, mudstone powder, glass cullet which is combined with swell and flux etc. after made into lightweight granular aggregate of different sizes through the processes of mixing and rotating granulation. The lightweight aggregate are dried in the shade before drying by oven, and sintered at a temperature increased by 5℃/min. The sintering temperature is set at 800℃, 900℃ and 1000℃, incineration fly ash is set to 20% and 30%,swell is set to 3% and 3%~15%, flux is set to 3% and 3%~15%, base mechanics features of light weight aggregate through tests of compressive strength, density, water absorption and scanning electron microscopy, with discussion made on the impact of the contents of swell and flux, on the compression strength, density, water absorption, and physical properties. The sintering temperature in this study is controlled in consideration of energy efficiency and reduction of carbon dioxide emission, and boric acid and calcium carbonate are used as swell, and alumina, iron oxide, sodium bicarbonate as flux to produce an adequate swelling environment to achieve the higher strength and lower density by increasing the viscidity and reducing the swelling temperature. Experimental results have proven that: (1)the major crystalline compound for materials like incineration fly ash and glass cullet, etc. is SiO2, and the minor crystalline compounds of them are Al2O3, Fe2O3, CaO, MgO, K2O and Na2O, which are suitable to be made into lightweight aggregate. (2) if the incineration fly ash is 20%, when the vesicant adopts boric acid at the fixed content of 3% and that of the fusing agent is 3%~15%, as for the mixture ration of IFA20-M20-G54-B3-Al 3~IFA20-M20-G42-B3-NaH15, etc., in general, the requirements for green building materials can’t be met even at the firing temperature of 1000°C, where, the mixing intensity of IFA20-M20-G42-B3-Fe 15 is the highest, in addition to IFA20-M20-G42-B3-Fe15, IFA20-M20-G42-B3-NaH15 rations, the others are unable to meet the green building requirements. (3) if the incineration fly ash is 20%, when the vesicant adopts calcium carbonate of 3%~15% and that of the fusing agent is fixed at 3%, as for the mixture ration of IFA20-M20-G54-Ca3-Al 3~IFA20-M20-G42-Ca15-NaH3, etc., the requirements for green building materials can’t be met at the firing temperature of 1000°C, where, the mixing intensity of IFA20-M20-G54-Ca3-Fe 3 is the highest. (4) if the incineration fly ash is increased to 30%, when the vesicant adopts boric acid at the fixed content of 3% and that of the fusing agent is 3%~15%, as for the mixture ration of IFA30-M20-G44-B3-Al 3~IFA30-M20-G32-B3-NaH15, the requirements for green building materials can’t be met even at the firing temperature of 900°C, where, the mixing intensity of IFA30-M20-G44-B3-Fe 3 is the highest. (5) if the incineration fly ash is increased to 30%, when the vesicant still adopts boric acid is 3%~15% and that of the fusing agent at the fixed content of 3%, as for the mixture ration of IFA30-M20-G44-B3-Al 3~IFA30-M20-G32-B15-NaH3, in general, the requirements for green building materials can’t be met even at the firing temperature of 1000°C, where, the mixing intensity of IFA30-M20-G44-B3-Fe 3 is the highest. (6) if the content of vesicant is fixed at 3% and that of the fusing agent is 3%~15%, when the content of the incineration fly ash is 20%, the compression strength and density are high, but water absorption is low; when boric acid is adopted as the vesicant, the intensity is high, the density and water absorption are low more significant, however, the dosage shall not exceed 9%. Keywords: Incineration Fly Ash, Mudstone Powder, Glass Cullet, Swell, Flux, Rotating Granulation. 王金鐘 2010 學位論文 ; thesis 83 zh-TW |
collection |
NDLTD |
language |
zh-TW |
format |
Others
|
sources |
NDLTD |
description |
碩士 === 正修科技大學 === 營建工程研究所 === 98 === Abstract
This study is to make use of the treated incineration fly ash, mudstone powder, glass cullet which is combined with swell and flux etc. after made into lightweight granular aggregate of different sizes through the processes of mixing and rotating granulation. The lightweight aggregate are dried in the shade before drying by oven, and sintered at a temperature increased by 5℃/min. The sintering temperature is set at 800℃, 900℃ and 1000℃, incineration fly ash is set to 20% and 30%,swell is set to 3% and 3%~15%, flux is set to 3% and 3%~15%, base mechanics features of light weight aggregate through tests of compressive strength, density, water absorption and scanning electron microscopy, with discussion made on the impact of the contents of swell and flux, on the compression strength, density, water absorption, and physical properties.
The sintering temperature in this study is controlled in consideration of energy efficiency and reduction of carbon dioxide emission, and boric acid and calcium carbonate are used as swell, and alumina, iron oxide, sodium bicarbonate as flux to produce an adequate swelling environment to achieve the higher strength and lower density by increasing the viscidity and reducing the swelling temperature.
Experimental results have proven that: (1)the major crystalline compound for materials like incineration fly ash and glass cullet, etc. is SiO2, and the minor crystalline compounds of them are Al2O3, Fe2O3, CaO, MgO, K2O and Na2O, which are suitable to be made into lightweight aggregate. (2) if the incineration fly ash is 20%, when the vesicant adopts boric acid at the fixed content of 3% and that of the fusing agent is 3%~15%, as for the mixture ration of IFA20-M20-G54-B3-Al 3~IFA20-M20-G42-B3-NaH15, etc., in general, the requirements for green building materials can’t be met even at the firing temperature of 1000°C, where, the mixing intensity of IFA20-M20-G42-B3-Fe 15 is the highest, in addition to IFA20-M20-G42-B3-Fe15, IFA20-M20-G42-B3-NaH15 rations, the others are unable to meet the green building requirements. (3) if the incineration fly ash is 20%, when the vesicant adopts calcium carbonate of 3%~15% and that of the fusing agent is fixed at 3%, as for the mixture ration of IFA20-M20-G54-Ca3-Al 3~IFA20-M20-G42-Ca15-NaH3, etc., the requirements for green building materials can’t be met at the firing temperature of 1000°C, where, the mixing intensity of IFA20-M20-G54-Ca3-Fe 3 is the highest. (4) if the incineration fly ash is increased to 30%, when the vesicant adopts boric acid at the fixed content of 3% and that of the fusing agent is 3%~15%, as for the mixture ration of IFA30-M20-G44-B3-Al 3~IFA30-M20-G32-B3-NaH15, the requirements for green building materials can’t be met even at the firing temperature of 900°C, where, the mixing intensity of IFA30-M20-G44-B3-Fe 3 is the highest. (5) if the incineration fly ash is increased to 30%, when the vesicant still adopts boric acid is 3%~15% and that of the fusing agent at the fixed content of 3%, as for the mixture ration of IFA30-M20-G44-B3-Al 3~IFA30-M20-G32-B15-NaH3, in general, the requirements for green building materials can’t be met even at the firing temperature of 1000°C, where, the mixing intensity of IFA30-M20-G44-B3-Fe 3 is the highest. (6) if the content of vesicant is fixed at 3% and that of the fusing agent is 3%~15%, when the content of the incineration fly ash is 20%, the compression strength and density are high, but water absorption is low; when boric acid is adopted as the vesicant, the intensity is high, the density and water absorption are low more significant, however, the dosage shall not exceed 9%.
Keywords: Incineration Fly Ash, Mudstone Powder, Glass Cullet, Swell, Flux, Rotating Granulation.
|
author2 |
王金鐘 |
author_facet |
王金鐘 Huang, Qun-xiang 黃群翔 |
author |
Huang, Qun-xiang 黃群翔 |
spellingShingle |
Huang, Qun-xiang 黃群翔 焚化飛灰燒製成輕質骨材及其工程性質之研究 |
author_sort |
Huang, Qun-xiang |
title |
焚化飛灰燒製成輕質骨材及其工程性質之研究 |
title_short |
焚化飛灰燒製成輕質骨材及其工程性質之研究 |
title_full |
焚化飛灰燒製成輕質骨材及其工程性質之研究 |
title_fullStr |
焚化飛灰燒製成輕質骨材及其工程性質之研究 |
title_full_unstemmed |
焚化飛灰燒製成輕質骨材及其工程性質之研究 |
title_sort |
焚化飛灰燒製成輕質骨材及其工程性質之研究 |
publishDate |
2010 |
url |
http://ndltd.ncl.edu.tw/handle/79154414244238351502 |
work_keys_str_mv |
AT huangqunxiang fénhuàfēihuīshāozhìchéngqīngzhìgǔcáijíqígōngchéngxìngzhìzhīyánjiū AT huángqúnxiáng fénhuàfēihuīshāozhìchéngqīngzhìgǔcáijíqígōngchéngxìngzhìzhīyánjiū |
_version_ |
1718113303576707072 |