The Study of Encapsulation for Longevity of Organic Electroluminescent Devices with Passivation Layer
碩士 === 國立屏東科技大學 === 機械工程系所 === 98 === In this work, we deposited the passivation layer on devices by vacuum evaporation to investigate the effect of OLED with passivation layer and encapsulation. The device structure was ITO/NPB/Alq3/LiF/Al. A m-MTDATA/SiO2 passivation layer was deposited to separat...
Main Authors: | , |
---|---|
Other Authors: | |
Format: | Others |
Language: | zh-TW |
Published: |
2010
|
Online Access: | http://ndltd.ncl.edu.tw/handle/60228739830794034960 |
id |
ndltd-TW-098NPUS5489035 |
---|---|
record_format |
oai_dc |
spelling |
ndltd-TW-098NPUS54890352016-12-22T04:18:19Z http://ndltd.ncl.edu.tw/handle/60228739830794034960 The Study of Encapsulation for Longevity of Organic Electroluminescent Devices with Passivation Layer 保護層用於有機電激發光元件封裝壽命之研究 Mu-Shian Chen 陳牧賢 碩士 國立屏東科技大學 機械工程系所 98 In this work, we deposited the passivation layer on devices by vacuum evaporation to investigate the effect of OLED with passivation layer and encapsulation. The device structure was ITO/NPB/Alq3/LiF/Al. A m-MTDATA/SiO2 passivation layer was deposited to separate hydrosphere and prevent the degradation. The electrical and emissive properties of device with and without passivation layer are compared and the degradation was observed. In this case, a passivation layer process did not influence the electrical and emissive characteristic of device and enhanced the lifetime in the air. The current density of device was set at 10 mA/cm2 and the initial luminance was 300 cd/m2. Under R.H 50 % and R.H 70 % in the air, the half-life of device with passivation layer improves by 6 times and 5 times, respectively. Besides, the half-life of device with passivation layer and encapsulation improves by 24 times and 27 times, respectively. According to the experiment results, we conclude that adding a passivation layer in the encapsulation device effectively separates hydrosphere and enhances the device lifetime. Nyen-Ts Chen 陳念慈 2010 學位論文 ; thesis 61 zh-TW |
collection |
NDLTD |
language |
zh-TW |
format |
Others
|
sources |
NDLTD |
description |
碩士 === 國立屏東科技大學 === 機械工程系所 === 98 === In this work, we deposited the passivation layer on devices by vacuum evaporation to investigate the effect of OLED with passivation layer and encapsulation. The device structure was ITO/NPB/Alq3/LiF/Al. A m-MTDATA/SiO2 passivation layer was deposited to separate hydrosphere and prevent the degradation. The electrical and emissive properties of device with and without passivation layer are compared and the degradation was observed.
In this case, a passivation layer process did not influence the electrical and emissive characteristic of device and enhanced the lifetime in the air. The current density of device was set at 10 mA/cm2 and the initial luminance was 300 cd/m2. Under R.H 50 % and R.H 70 % in the air, the half-life of device with passivation layer improves by 6 times and 5 times, respectively. Besides, the half-life of device with passivation layer and encapsulation improves by 24 times and 27 times, respectively.
According to the experiment results, we conclude that adding a passivation layer in the encapsulation device effectively separates hydrosphere and enhances the device lifetime.
|
author2 |
Nyen-Ts Chen |
author_facet |
Nyen-Ts Chen Mu-Shian Chen 陳牧賢 |
author |
Mu-Shian Chen 陳牧賢 |
spellingShingle |
Mu-Shian Chen 陳牧賢 The Study of Encapsulation for Longevity of Organic Electroluminescent Devices with Passivation Layer |
author_sort |
Mu-Shian Chen |
title |
The Study of Encapsulation for Longevity of Organic Electroluminescent Devices with Passivation Layer |
title_short |
The Study of Encapsulation for Longevity of Organic Electroluminescent Devices with Passivation Layer |
title_full |
The Study of Encapsulation for Longevity of Organic Electroluminescent Devices with Passivation Layer |
title_fullStr |
The Study of Encapsulation for Longevity of Organic Electroluminescent Devices with Passivation Layer |
title_full_unstemmed |
The Study of Encapsulation for Longevity of Organic Electroluminescent Devices with Passivation Layer |
title_sort |
study of encapsulation for longevity of organic electroluminescent devices with passivation layer |
publishDate |
2010 |
url |
http://ndltd.ncl.edu.tw/handle/60228739830794034960 |
work_keys_str_mv |
AT mushianchen thestudyofencapsulationforlongevityoforganicelectroluminescentdeviceswithpassivationlayer AT chénmùxián thestudyofencapsulationforlongevityoforganicelectroluminescentdeviceswithpassivationlayer AT mushianchen bǎohùcéngyòngyúyǒujīdiànjīfāguāngyuánjiànfēngzhuāngshòumìngzhīyánjiū AT chénmùxián bǎohùcéngyòngyúyǒujīdiànjīfāguāngyuánjiànfēngzhuāngshòumìngzhīyánjiū AT mushianchen studyofencapsulationforlongevityoforganicelectroluminescentdeviceswithpassivationlayer AT chénmùxián studyofencapsulationforlongevityoforganicelectroluminescentdeviceswithpassivationlayer |
_version_ |
1718404042514759680 |