Synthesis of Soluble Organic Thin film transistors.
碩士 === 國立中央大學 === 化學研究所 === 99 === Asymmetric fused thiophene compound (11) was synthesized by “one-pot” reaction. Based on compound (11), derivatives (1) and (2) have been developed. Both compounds exhibit p-type field-effect performances with mobility of 0.026 and 9x10-4 cm2/Vs via vacuum evaporat...
Main Authors: | , |
---|---|
Other Authors: | |
Format: | Others |
Language: | zh-TW |
Published: |
2011
|
Online Access: | http://ndltd.ncl.edu.tw/handle/40109234357727157180 |
id |
ndltd-TW-099NCU05065082 |
---|---|
record_format |
oai_dc |
spelling |
ndltd-TW-099NCU050650822017-07-07T04:31:05Z http://ndltd.ncl.edu.tw/handle/40109234357727157180 Synthesis of Soluble Organic Thin film transistors. 有機薄膜電晶體材料苯三併環噻吩及可溶性聯噻吩衍生物之開發 Chia-Ming Yeh 葉佳明 碩士 國立中央大學 化學研究所 99 Asymmetric fused thiophene compound (11) was synthesized by “one-pot” reaction. Based on compound (11), derivatives (1) and (2) have been developed. Both compounds exhibit p-type field-effect performances with mobility of 0.026 and 9x10-4 cm2/Vs via vacuum evaporation, respectively. Compounds (3) ~ (9) have been successfully developed based on bithiophene compound (18). Preparation of soluble compound (18) has been improved with better yield. Compounds (6), (7), and (8) exhibit good field-effect performances with high mobility of 0.15, 0.38, and 0.24 cm2/Vs via solution process, respectively. All of these new semiconductor materials exhibit good stability under light, air, and thermal conditions. Ming-Chou Chen 陳銘洲 2011 學位論文 ; thesis 163 zh-TW |
collection |
NDLTD |
language |
zh-TW |
format |
Others
|
sources |
NDLTD |
description |
碩士 === 國立中央大學 === 化學研究所 === 99 === Asymmetric fused thiophene compound (11) was synthesized by “one-pot” reaction. Based on compound (11), derivatives (1) and (2) have been developed. Both compounds exhibit p-type field-effect performances with mobility of 0.026 and 9x10-4 cm2/Vs via vacuum evaporation, respectively.
Compounds (3) ~ (9) have been successfully developed based on bithiophene compound (18). Preparation of soluble compound (18) has been improved with better yield. Compounds (6), (7), and (8) exhibit good field-effect performances with high mobility of 0.15, 0.38, and 0.24 cm2/Vs via solution process, respectively. All of these new semiconductor materials exhibit good stability under light, air, and thermal conditions.
|
author2 |
Ming-Chou Chen |
author_facet |
Ming-Chou Chen Chia-Ming Yeh 葉佳明 |
author |
Chia-Ming Yeh 葉佳明 |
spellingShingle |
Chia-Ming Yeh 葉佳明 Synthesis of Soluble Organic Thin film transistors. |
author_sort |
Chia-Ming Yeh |
title |
Synthesis of Soluble Organic Thin film transistors. |
title_short |
Synthesis of Soluble Organic Thin film transistors. |
title_full |
Synthesis of Soluble Organic Thin film transistors. |
title_fullStr |
Synthesis of Soluble Organic Thin film transistors. |
title_full_unstemmed |
Synthesis of Soluble Organic Thin film transistors. |
title_sort |
synthesis of soluble organic thin film transistors. |
publishDate |
2011 |
url |
http://ndltd.ncl.edu.tw/handle/40109234357727157180 |
work_keys_str_mv |
AT chiamingyeh synthesisofsolubleorganicthinfilmtransistors AT yèjiāmíng synthesisofsolubleorganicthinfilmtransistors AT chiamingyeh yǒujībáomódiànjīngtǐcáiliàoběnsānbìnghuánsāifēnjíkěróngxìngliánsāifēnyǎnshēngwùzhīkāifā AT yèjiāmíng yǒujībáomódiànjīngtǐcáiliàoběnsānbìnghuánsāifēnjíkěróngxìngliánsāifēnyǎnshēngwùzhīkāifā |
_version_ |
1718492124467429376 |