Size effect study of DyMn2O5 nanorods
碩士 === 中原大學 === 物理研究所 === 100 === Two series of DyMn2O5 nanorods were synthesized by hydrothermal method in different time. They have different length by long axis with different annealing temperature. X-ray diffraction revealed the crystal structures are formed as orthorhombic Pbam phase for ea...
Main Authors: | , |
---|---|
Other Authors: | |
Format: | Others |
Language: | zh-TW |
Published: |
2012
|
Online Access: | http://ndltd.ncl.edu.tw/handle/53899004961614738039 |
Summary: | 碩士 === 中原大學 === 物理研究所 === 100 === Two series of DyMn2O5 nanorods were synthesized by hydrothermal method in different time. They have different length by long axis with different annealing temperature. X-ray diffraction revealed the crystal structures are formed as orthorhombic Pbam phase for each sample. SAED results show that the long side of nanorods is parallel to c axis for all three samples. Magnetic ac susceptibility measurements were used to determinate magnetic properties. Curie-Weiss law is employed to analysis the ac magnetic susceptibility curves. It is found that Néel temperature is increased with increasing length. Antiferromagnetic peaks at around 38 and 43 K were only observed as length longer than 46 nm, which implied a critical length of magnetic ordering at around 50 nm.
|
---|