Properties and Production of Waste-Glass Binders Activated without Alkalis
碩士 === 國立成功大學 === 土木工程學系碩博士班 === 100 === Alkali-activating solution is typically used in the production of inorganic polymers which are binders with higher compressive strength but lower energy-consumption. As a result of that, the cost of inorganic polymeric binder increases and its impact on our...
Main Authors: | , |
---|---|
Other Authors: | |
Format: | Others |
Language: | zh-TW |
Published: |
2012
|
Online Access: | http://ndltd.ncl.edu.tw/handle/95596934248881206131 |
id |
ndltd-TW-100NCKU5015055 |
---|---|
record_format |
oai_dc |
spelling |
ndltd-TW-100NCKU50150552015-10-13T21:38:02Z http://ndltd.ncl.edu.tw/handle/95596934248881206131 Properties and Production of Waste-Glass Binders Activated without Alkalis 無鹼激發廢玻璃膠結材之研究 Yu-MeiChiu 邱友梅 碩士 國立成功大學 土木工程學系碩博士班 100 Alkali-activating solution is typically used in the production of inorganic polymers which are binders with higher compressive strength but lower energy-consumption. As a result of that, the cost of inorganic polymeric binder increases and its impact on our environmental ecology could be severe. To develop low energy-consumption binders and to reduce the amount of recycled glass, waste glass was activated without alkalis in this study. By using an appropriate process of aging and curing, the compressive strength of inorganic polymeric binders can be up to 100MPa. At first, the effects of aging and curing conditions on the compressive strengths of waste-glass binders activated without alkalis are evaluated to propose an appropriate aging and curing process. Then, the relationship between in-service temperature and reaction rate in the well-known Arrhenius theory can be employed to empirically determine the activation energy of waste-glass binders activated without alkalis. In addition, the mechanism of curing can be identified by using Mori and Minegishi method. Finally, the experimental results of FTIR and dissolution tests indicate that the microstructure of waste-glass binders activated without alkalis is similar to that of sodium-lime glass. Jong-Shin Huang 黃忠信 2012 學位論文 ; thesis 71 zh-TW |
collection |
NDLTD |
language |
zh-TW |
format |
Others
|
sources |
NDLTD |
description |
碩士 === 國立成功大學 === 土木工程學系碩博士班 === 100 === Alkali-activating solution is typically used in the production of inorganic polymers which are binders with higher compressive strength but lower energy-consumption. As a result of that, the cost of inorganic polymeric binder increases and its impact on our environmental ecology could be severe. To develop low energy-consumption binders and to reduce the amount of recycled glass, waste glass was activated without alkalis in this study. By using an appropriate process of aging and curing, the compressive strength of inorganic polymeric binders can be up to 100MPa. At first, the effects of aging and curing conditions on the compressive strengths of waste-glass binders activated without alkalis are evaluated to propose an appropriate aging and curing process. Then, the relationship between in-service temperature and reaction rate in the well-known Arrhenius theory can be employed to empirically determine the activation energy of waste-glass binders activated without alkalis. In addition, the mechanism of curing can be identified by using Mori and Minegishi method. Finally, the experimental results of FTIR and dissolution tests indicate that the microstructure of waste-glass binders activated without alkalis is similar to that of sodium-lime glass.
|
author2 |
Jong-Shin Huang |
author_facet |
Jong-Shin Huang Yu-MeiChiu 邱友梅 |
author |
Yu-MeiChiu 邱友梅 |
spellingShingle |
Yu-MeiChiu 邱友梅 Properties and Production of Waste-Glass Binders Activated without Alkalis |
author_sort |
Yu-MeiChiu |
title |
Properties and Production of Waste-Glass Binders Activated without Alkalis |
title_short |
Properties and Production of Waste-Glass Binders Activated without Alkalis |
title_full |
Properties and Production of Waste-Glass Binders Activated without Alkalis |
title_fullStr |
Properties and Production of Waste-Glass Binders Activated without Alkalis |
title_full_unstemmed |
Properties and Production of Waste-Glass Binders Activated without Alkalis |
title_sort |
properties and production of waste-glass binders activated without alkalis |
publishDate |
2012 |
url |
http://ndltd.ncl.edu.tw/handle/95596934248881206131 |
work_keys_str_mv |
AT yumeichiu propertiesandproductionofwasteglassbindersactivatedwithoutalkalis AT qiūyǒuméi propertiesandproductionofwasteglassbindersactivatedwithoutalkalis AT yumeichiu wújiǎnjīfāfèibōlíjiāojiécáizhīyánjiū AT qiūyǒuméi wújiǎnjīfāfèibōlíjiāojiécáizhīyánjiū |
_version_ |
1718066532407312384 |