The Study of Transparent Conductive Nanotubes Film on Flexible Substrate
碩士 === 國立雲林科技大學 === 電子與光電工程研究所碩士班 === 100 === This study investigated the application of single-wall carbon nanotubes ( SWCNTs) on transparent conducting film. The SWCNTs films deposited on the flexible substrate using dip-coating. The major issue was studying the time and temperature of sulfuric ac...
Main Authors: | , |
---|---|
Other Authors: | |
Format: | Others |
Language: | zh-TW |
Published: |
2012
|
Online Access: | http://ndltd.ncl.edu.tw/handle/06010039107609312173 |
id |
ndltd-TW-100YUNT5393060 |
---|---|
record_format |
oai_dc |
spelling |
ndltd-TW-100YUNT53930602015-10-13T21:56:00Z http://ndltd.ncl.edu.tw/handle/06010039107609312173 The Study of Transparent Conductive Nanotubes Film on Flexible Substrate 奈米碳管透明導電膜在軟性基板之研究 Hsuan-Yi Chiu 邱煊奕 碩士 國立雲林科技大學 電子與光電工程研究所碩士班 100 This study investigated the application of single-wall carbon nanotubes ( SWCNTs) on transparent conducting film. The SWCNTs films deposited on the flexible substrate using dip-coating. The major issue was studying the time and temperature of sulfuric acid effect on the purification of SWCNTs. The post-treatment of etching dispersion and how to affect the optical and sheet resistance were always considered. The results showed that the sheet resistance of SWCNTs with 12 hrs purification was higher than that without purification, but over 12 hrs the sheet resistance was lower than that without purification. The sheet resistances of SWCNTs at purification temperature of 160°C and 100°C were higher than as-prepared SWCNTs, and the lowest sheet resistance of SWCNTs at purification temperature of 120°C. Simultaneously, the dispersion combined with both the functional group consisting of acetic acid (-COOH) could make SWCNTs more purify and reduced the amorphous carbon. Purification of sulfuric acid at temperature of 120°C and time of 24 hrs had the good performance on optical and electricity for SWCNTs film and the sheet resistance of SWCNTs film could reach 781 Ω/sq. at transmittance of 70%. This study successfully explained the mechanism of the purification of the dispersing and acid destroying for SWCNTs by using Raman spectrum. An optimized acid purification was used to improve the transparent and electricity on the flexible substrate with SWCNTs. Hsi-Chao Chen 陳錫釗 2012 學位論文 ; thesis 64 zh-TW |
collection |
NDLTD |
language |
zh-TW |
format |
Others
|
sources |
NDLTD |
description |
碩士 === 國立雲林科技大學 === 電子與光電工程研究所碩士班 === 100 === This study investigated the application of single-wall carbon nanotubes ( SWCNTs) on transparent conducting film. The SWCNTs films deposited on the flexible substrate using dip-coating. The major issue was studying the time and temperature of sulfuric acid effect on the purification of SWCNTs. The post-treatment of etching dispersion and how to affect the optical and sheet resistance were always considered. The results showed that the sheet resistance of SWCNTs with 12 hrs purification was higher than that without purification, but over 12 hrs the sheet resistance was lower than that without purification. The sheet resistances of SWCNTs at purification temperature of 160°C and 100°C were higher than as-prepared SWCNTs, and the lowest sheet resistance of SWCNTs at purification temperature of 120°C. Simultaneously, the dispersion combined with both the functional group consisting of acetic acid (-COOH) could make SWCNTs more purify and reduced the amorphous carbon. Purification of sulfuric acid at temperature of 120°C and time of 24 hrs had the good performance on optical and electricity for SWCNTs film and the sheet resistance of SWCNTs film could reach 781 Ω/sq. at transmittance of 70%. This study successfully explained the mechanism of the purification of the dispersing and acid destroying for SWCNTs by using Raman spectrum. An optimized acid purification was used to improve the transparent and electricity on the flexible substrate with SWCNTs.
|
author2 |
Hsi-Chao Chen |
author_facet |
Hsi-Chao Chen Hsuan-Yi Chiu 邱煊奕 |
author |
Hsuan-Yi Chiu 邱煊奕 |
spellingShingle |
Hsuan-Yi Chiu 邱煊奕 The Study of Transparent Conductive Nanotubes Film on Flexible Substrate |
author_sort |
Hsuan-Yi Chiu |
title |
The Study of Transparent Conductive Nanotubes Film on Flexible Substrate |
title_short |
The Study of Transparent Conductive Nanotubes Film on Flexible Substrate |
title_full |
The Study of Transparent Conductive Nanotubes Film on Flexible Substrate |
title_fullStr |
The Study of Transparent Conductive Nanotubes Film on Flexible Substrate |
title_full_unstemmed |
The Study of Transparent Conductive Nanotubes Film on Flexible Substrate |
title_sort |
study of transparent conductive nanotubes film on flexible substrate |
publishDate |
2012 |
url |
http://ndltd.ncl.edu.tw/handle/06010039107609312173 |
work_keys_str_mv |
AT hsuanyichiu thestudyoftransparentconductivenanotubesfilmonflexiblesubstrate AT qiūxuānyì thestudyoftransparentconductivenanotubesfilmonflexiblesubstrate AT hsuanyichiu nàimǐtànguǎntòumíngdǎodiànmózàiruǎnxìngjībǎnzhīyánjiū AT qiūxuānyì nàimǐtànguǎntòumíngdǎodiànmózàiruǎnxìngjībǎnzhīyánjiū AT hsuanyichiu studyoftransparentconductivenanotubesfilmonflexiblesubstrate AT qiūxuānyì studyoftransparentconductivenanotubesfilmonflexiblesubstrate |
_version_ |
1718070737739186176 |