Effect of reinforcement size on the mechanical properties of as cast and extruded AZ61/SiCp magnesium matrix composites
碩士 === 國立臺灣科技大學 === 機械工程系 === 101 === The mechanical behavior of magnesium metal matrix composites (Mg MMCs) are superior to those of the pure metal alloy. By adding the reinforcement, such as particles, short fibers, or continuous fibers, into the metal matrix can improve the composite’s mechanical...
Main Authors: | , |
---|---|
Other Authors: | |
Format: | Others |
Language: | zh-TW |
Published: |
2013
|
Online Access: | http://ndltd.ncl.edu.tw/handle/59446694578289122457 |
id |
ndltd-TW-101NTUS5489183 |
---|---|
record_format |
oai_dc |
spelling |
ndltd-TW-101NTUS54891832016-03-21T04:28:04Z http://ndltd.ncl.edu.tw/handle/59446694578289122457 Effect of reinforcement size on the mechanical properties of as cast and extruded AZ61/SiCp magnesium matrix composites 強化相粒徑對AZ61/SiCp鎂基複合材料鑄錠及擠型材之機械性質影響的研究 Chien-Chung Huang 黃建忠 碩士 國立臺灣科技大學 機械工程系 101 The mechanical behavior of magnesium metal matrix composites (Mg MMCs) are superior to those of the pure metal alloy. By adding the reinforcement, such as particles, short fibers, or continuous fibers, into the metal matrix can improve the composite’s mechanical properties. Three different particle size of SiCp are dissolved into AZ61 by the stir-casting method, and then the Mg-based composite is fabricated. Before extrusion, solid solution treatment was conducted to improve the ductility of the material. Eventually, the mechanical properties of the composite before and after the extrusion with aging treatment are discussed. The results shows that the ultimate tensile strength, yielding strength, ductility and hardness of magnesium matrix composites will decrease with increasing the size of reinforcement. The ultimate tensile strength, yielding strength, ductility and hardness of AZ61/5 wt% SiCp/10 μm ingot are 146.7 MPa, 66.6 MPa, 3.8% and 59.4 HV, respectively. Compared with the AZ61/5 wt% SiCp/1 μm ingot were reduced 19.2%、10.7%、36.7%、2.5%. For the extrusion rod, AZ61/5 wt% SiCp/1 μm exhibits better mechanical properties, which will decrease with increasing the reinforcement size. The ultimate strength, yielding strength, ductility and hardness are 316.0 MPa, 147.5 MPa, 16.6% and 69.1 HV, respectively. In addition, aging treatment will enhance the ultimate strength, yielding strength and hardness of rods. In this study, microstructure of AZ61/5 wt% SiCp/10 μm ingot shows Mg2Si compound at the grain boundaries after solid solution treatment. The Mg2Si compound will affect the mechanical properties of magnesium matrix composite. From the experiment results, the mechanical properties decreased greatly with the reinforcement size of 10 μm. Song-Jeng Huang 黃崧任 2013 學位論文 ; thesis 106 zh-TW |
collection |
NDLTD |
language |
zh-TW |
format |
Others
|
sources |
NDLTD |
description |
碩士 === 國立臺灣科技大學 === 機械工程系 === 101 === The mechanical behavior of magnesium metal matrix composites (Mg MMCs) are superior to those of the pure metal alloy. By adding the reinforcement, such as particles, short fibers, or continuous fibers, into the metal matrix can improve the composite’s mechanical properties. Three different particle size of SiCp are dissolved into AZ61 by the stir-casting method, and then the Mg-based composite is fabricated. Before extrusion, solid solution treatment was conducted to improve the ductility of the material. Eventually, the mechanical properties of the composite before and after the extrusion with aging treatment are discussed.
The results shows that the ultimate tensile strength, yielding strength, ductility and hardness of magnesium matrix composites will decrease with increasing the size of reinforcement. The ultimate tensile strength, yielding strength, ductility and hardness of AZ61/5 wt% SiCp/10 μm ingot are 146.7 MPa, 66.6 MPa, 3.8% and 59.4 HV, respectively. Compared with the AZ61/5 wt% SiCp/1 μm ingot were reduced 19.2%、10.7%、36.7%、2.5%. For the extrusion rod, AZ61/5 wt% SiCp/1 μm exhibits better mechanical properties, which will decrease with increasing the reinforcement size. The ultimate strength, yielding strength, ductility and hardness are 316.0 MPa, 147.5 MPa, 16.6% and 69.1 HV, respectively. In addition, aging treatment will enhance the ultimate strength, yielding strength and hardness of rods.
In this study, microstructure of AZ61/5 wt% SiCp/10 μm ingot shows Mg2Si compound at the grain boundaries after solid solution treatment. The Mg2Si compound will affect the mechanical properties of magnesium matrix composite. From the experiment results, the mechanical properties decreased greatly with the reinforcement size of 10 μm.
|
author2 |
Song-Jeng Huang |
author_facet |
Song-Jeng Huang Chien-Chung Huang 黃建忠 |
author |
Chien-Chung Huang 黃建忠 |
spellingShingle |
Chien-Chung Huang 黃建忠 Effect of reinforcement size on the mechanical properties of as cast and extruded AZ61/SiCp magnesium matrix composites |
author_sort |
Chien-Chung Huang |
title |
Effect of reinforcement size on the mechanical properties of as cast and extruded AZ61/SiCp magnesium matrix composites |
title_short |
Effect of reinforcement size on the mechanical properties of as cast and extruded AZ61/SiCp magnesium matrix composites |
title_full |
Effect of reinforcement size on the mechanical properties of as cast and extruded AZ61/SiCp magnesium matrix composites |
title_fullStr |
Effect of reinforcement size on the mechanical properties of as cast and extruded AZ61/SiCp magnesium matrix composites |
title_full_unstemmed |
Effect of reinforcement size on the mechanical properties of as cast and extruded AZ61/SiCp magnesium matrix composites |
title_sort |
effect of reinforcement size on the mechanical properties of as cast and extruded az61/sicp magnesium matrix composites |
publishDate |
2013 |
url |
http://ndltd.ncl.edu.tw/handle/59446694578289122457 |
work_keys_str_mv |
AT chienchunghuang effectofreinforcementsizeonthemechanicalpropertiesofascastandextrudedaz61sicpmagnesiummatrixcomposites AT huángjiànzhōng effectofreinforcementsizeonthemechanicalpropertiesofascastandextrudedaz61sicpmagnesiummatrixcomposites AT chienchunghuang qiánghuàxiānglìjìngduìaz61sicpměijīfùhécáiliàozhùdìngjíjǐxíngcáizhījīxièxìngzhìyǐngxiǎngdeyánjiū AT huángjiànzhōng qiánghuàxiānglìjìngduìaz61sicpměijīfùhécáiliàozhùdìngjíjǐxíngcáizhījīxièxìngzhìyǐngxiǎngdeyánjiū |
_version_ |
1718210403619569664 |