Effects of Pre-delamination and Fiber Adding to Waterproof Material on Crack
碩士 === 國立雲林科技大學 === 營建工程系碩士班 === 101 === Due to temperature fluctuating , water-based waterproof material cracks and delaminates easily , which becomes a major engineering issue these days. In this study fiber is added to the water-based waterproof material trying to enlarge the tension failure stra...
Main Authors: | Ching-Wen Chuang, 莊景文 |
---|---|
Other Authors: | Cho-Liang Tsai |
Format: | Others |
Language: | zh-TW |
Published: |
2013
|
Online Access: | http://ndltd.ncl.edu.tw/handle/71308522656691626260 |
Similar Items
-
A Study of Waterproof Reinforcement Layers for the Post-Cracking Behavior of Fiber Reinforced Concrete
by: Jung-Il Kim, et al.
Published: (2020-08-01) -
A Study of Fatigue Crack and Delamination Growth in Fiber-Metal Composite Laminate
by: Wang Yu-Hsin, et al.
Published: (1998) -
Impedance Properties of Paste Incorporating with Silica Fume and Waterproof MaterialImpedance Properties of Paste Incorporating with Silica Fume and Waterproof MaterialImpedance Properties of Paste Incorporating with Silica Fume and Waterproof Material
by: Ching-Hsi Chou, et al.
Published: (2010) -
Strain Concentration Ratio Analysis of Different Waterproofing Materials during Concrete Crack Movement
by: Kyu-hwan Oh, et al.
Published: (2021-08-01) -
A Mesoscale Model for Damage, Cracking and Delamination Prediction in Composite Materials
by: Bordeu, F., et al.
Published: (2010-12-01)