The application of the doped porous ceria and zirconia films by EB-PVD in the electrodes of SOFCs
博士 === 國立成功大學 === 材料科學及工程學系 === 102 === Yttrium doped porous zirconia film was deposited on 10 at.% samaria doped ceria by electron beam evaporator with assistance of glancing angle technique. La(Sr)MnO3-δ(LSM), La(Sr)CoFeO3-δ(LSCF) and Pt were deposited on it as upper layer to serve as cathode. In...
Main Authors: | , |
---|---|
Other Authors: | |
Format: | Others |
Language: | zh-TW |
Published: |
2014
|
Online Access: | http://ndltd.ncl.edu.tw/handle/90866399206334502657 |
id |
ndltd-TW-102NCKU5159053 |
---|---|
record_format |
oai_dc |
spelling |
ndltd-TW-102NCKU51590532016-03-07T04:11:02Z http://ndltd.ncl.edu.tw/handle/90866399206334502657 The application of the doped porous ceria and zirconia films by EB-PVD in the electrodes of SOFCs 以電子束蒸鍍成長多孔氧化鋯與氧化鈰應用於固態燃料電池電極 Ming-HsiuWu 吳明修 博士 國立成功大學 材料科學及工程學系 102 Yttrium doped porous zirconia film was deposited on 10 at.% samaria doped ceria by electron beam evaporator with assistance of glancing angle technique. La(Sr)MnO3-δ(LSM), La(Sr)CoFeO3-δ(LSCF) and Pt were deposited on it as upper layer to serve as cathode. In the first part, YSZ/LSM bilayer exhibits lower resistance than LSM single layer on thick YSZ plate below 700℃. For intermediate temperature use, SDC plate and LSCF replaced the YSZ plate and LSM, but the power performance was 5.7 mWcm-2 at 600℃. In the second part, the LSCF film deposited by E-beam required further heat treatment, and cobalt oxide formed. For further examining this design, the interface of YSZ/SDC after 1000℃ heat treatment was observed under TEM and EDS. In the final part, different thickness of Pt deposited on YSZ columns with YSZ single crystal substrate, and the obtained highest power density was 20 mWcm-2 at 600℃. Jow-Lay Huang 黃肇瑞 2014 學位論文 ; thesis 111 zh-TW |
collection |
NDLTD |
language |
zh-TW |
format |
Others
|
sources |
NDLTD |
description |
博士 === 國立成功大學 === 材料科學及工程學系 === 102 === Yttrium doped porous zirconia film was deposited on 10 at.% samaria doped ceria by electron beam evaporator with assistance of glancing angle technique. La(Sr)MnO3-δ(LSM), La(Sr)CoFeO3-δ(LSCF) and Pt were deposited on it as upper layer to serve as cathode. In the first part, YSZ/LSM bilayer exhibits lower resistance than LSM single layer on thick YSZ plate below 700℃. For intermediate temperature use, SDC plate and LSCF replaced the YSZ plate and LSM, but the power performance was 5.7 mWcm-2 at 600℃. In the second part, the LSCF film deposited by E-beam required further heat treatment, and cobalt oxide formed. For further examining this design, the interface of YSZ/SDC after 1000℃ heat treatment was observed under TEM and EDS. In the final part, different thickness of Pt deposited on YSZ columns with YSZ single crystal substrate, and the obtained highest power density was 20 mWcm-2 at 600℃.
|
author2 |
Jow-Lay Huang |
author_facet |
Jow-Lay Huang Ming-HsiuWu 吳明修 |
author |
Ming-HsiuWu 吳明修 |
spellingShingle |
Ming-HsiuWu 吳明修 The application of the doped porous ceria and zirconia films by EB-PVD in the electrodes of SOFCs |
author_sort |
Ming-HsiuWu |
title |
The application of the doped porous ceria and zirconia films by EB-PVD in the electrodes of SOFCs |
title_short |
The application of the doped porous ceria and zirconia films by EB-PVD in the electrodes of SOFCs |
title_full |
The application of the doped porous ceria and zirconia films by EB-PVD in the electrodes of SOFCs |
title_fullStr |
The application of the doped porous ceria and zirconia films by EB-PVD in the electrodes of SOFCs |
title_full_unstemmed |
The application of the doped porous ceria and zirconia films by EB-PVD in the electrodes of SOFCs |
title_sort |
application of the doped porous ceria and zirconia films by eb-pvd in the electrodes of sofcs |
publishDate |
2014 |
url |
http://ndltd.ncl.edu.tw/handle/90866399206334502657 |
work_keys_str_mv |
AT minghsiuwu theapplicationofthedopedporousceriaandzirconiafilmsbyebpvdintheelectrodesofsofcs AT wúmíngxiū theapplicationofthedopedporousceriaandzirconiafilmsbyebpvdintheelectrodesofsofcs AT minghsiuwu yǐdiànzishùzhēngdùchéngzhǎngduōkǒngyǎnghuàgàoyǔyǎnghuàshìyīngyòngyúgùtàiránliàodiànchídiànjí AT wúmíngxiū yǐdiànzishùzhēngdùchéngzhǎngduōkǒngyǎnghuàgàoyǔyǎnghuàshìyīngyòngyúgùtàiránliàodiànchídiànjí AT minghsiuwu applicationofthedopedporousceriaandzirconiafilmsbyebpvdintheelectrodesofsofcs AT wúmíngxiū applicationofthedopedporousceriaandzirconiafilmsbyebpvdintheelectrodesofsofcs |
_version_ |
1718199410456788992 |