Washing Municipal Solid Waste Incinerator Bottom Ash and Water Filter Silt Resource Used as Controlled Low-Strength Materials
碩士 === 國立高雄應用科技大學 === 土木工程與防災科技研究所 === 103 === In this study is intended to produce controlled low-strength materials by the municipal solid waste incinerator (MSWI) to replace the natural aggregates, and water filter silt (WFS). Water-cement ratio was 1.5, 1.6, 1.7 and 2.0. The rest of the volume w...
Main Authors: | , |
---|---|
Other Authors: | |
Format: | Others |
Language: | zh-TW |
Published: |
2015
|
Online Access: | http://ndltd.ncl.edu.tw/handle/9whvb5 |
id |
ndltd-TW-103KUAS0653025 |
---|---|
record_format |
oai_dc |
spelling |
ndltd-TW-103KUAS06530252019-05-15T21:59:54Z http://ndltd.ncl.edu.tw/handle/9whvb5 Washing Municipal Solid Waste Incinerator Bottom Ash and Water Filter Silt Resource Used as Controlled Low-Strength Materials 水洗垃圾焚化底渣與水洗土資源化於控制性低強度材料 Zhen-Chang Gao 高振昌 碩士 國立高雄應用科技大學 土木工程與防災科技研究所 103 In this study is intended to produce controlled low-strength materials by the municipal solid waste incinerator (MSWI) to replace the natural aggregates, and water filter silt (WFS). Water-cement ratio was 1.5, 1.6, 1.7 and 2.0. The rest of the volume will be 0%, 25%, 50%, 75%, 100% of the fine MSWI instead of natural aggregates, and fine aggregate then were with 0%, 5%, 10%, and 20% of the instead of water filter silt. Due to replace the amount of water filter silt 20%, will absorb too much mixing water, so adjust Water-cement ratio to 2.0. Explore the fresh properties of slump, slump flow, tube flow, setting time and hardened properties compressive strength, ball drop. The results showed that all samples are in compliance with ASTM D6103 standards of slump/slump flow, flow consistency, slump flow are between 50-90 cm; tube flow are between 20-30 cm; ball drop test diameter were less than 7.6 cm, 28 days compressive strength are less 8.4MPa. All samples, with the addition 10% of water filter silt of lower early strength, setting time is longer, and Ball Drop in the critical value of test results. According to their fresh and hardened properties, the MSWI CLSM are feasible, but not add excessive water filter silt. Wen-Ten Kuo 郭文田 2015 學位論文 ; thesis 136 zh-TW |
collection |
NDLTD |
language |
zh-TW |
format |
Others
|
sources |
NDLTD |
description |
碩士 === 國立高雄應用科技大學 === 土木工程與防災科技研究所 === 103 === In this study is intended to produce controlled low-strength materials by the municipal solid waste incinerator (MSWI) to replace the natural aggregates, and water filter silt (WFS). Water-cement ratio was 1.5, 1.6, 1.7 and 2.0. The rest of the volume will be 0%, 25%, 50%, 75%, 100% of the fine MSWI instead of natural aggregates, and fine aggregate then were with 0%, 5%, 10%, and 20% of the instead of water filter silt. Due to replace the amount of water filter silt 20%, will absorb too much mixing water, so adjust Water-cement ratio to 2.0. Explore the fresh properties of slump, slump flow, tube flow, setting time and hardened properties compressive strength, ball drop. The results showed that all samples are in compliance with ASTM D6103 standards of slump/slump flow, flow consistency, slump flow are between 50-90 cm; tube flow are between 20-30 cm; ball drop test diameter were less than 7.6 cm, 28 days compressive strength are less 8.4MPa. All samples, with the addition 10% of water filter silt of lower early strength, setting time is longer, and Ball Drop in the critical value of test results. According to their fresh and hardened properties, the MSWI CLSM are feasible, but not add excessive water filter silt.
|
author2 |
Wen-Ten Kuo |
author_facet |
Wen-Ten Kuo Zhen-Chang Gao 高振昌 |
author |
Zhen-Chang Gao 高振昌 |
spellingShingle |
Zhen-Chang Gao 高振昌 Washing Municipal Solid Waste Incinerator Bottom Ash and Water Filter Silt Resource Used as Controlled Low-Strength Materials |
author_sort |
Zhen-Chang Gao |
title |
Washing Municipal Solid Waste Incinerator Bottom Ash and Water Filter Silt Resource Used as Controlled Low-Strength Materials |
title_short |
Washing Municipal Solid Waste Incinerator Bottom Ash and Water Filter Silt Resource Used as Controlled Low-Strength Materials |
title_full |
Washing Municipal Solid Waste Incinerator Bottom Ash and Water Filter Silt Resource Used as Controlled Low-Strength Materials |
title_fullStr |
Washing Municipal Solid Waste Incinerator Bottom Ash and Water Filter Silt Resource Used as Controlled Low-Strength Materials |
title_full_unstemmed |
Washing Municipal Solid Waste Incinerator Bottom Ash and Water Filter Silt Resource Used as Controlled Low-Strength Materials |
title_sort |
washing municipal solid waste incinerator bottom ash and water filter silt resource used as controlled low-strength materials |
publishDate |
2015 |
url |
http://ndltd.ncl.edu.tw/handle/9whvb5 |
work_keys_str_mv |
AT zhenchanggao washingmunicipalsolidwasteincineratorbottomashandwaterfiltersiltresourceusedascontrolledlowstrengthmaterials AT gāozhènchāng washingmunicipalsolidwasteincineratorbottomashandwaterfiltersiltresourceusedascontrolledlowstrengthmaterials AT zhenchanggao shuǐxǐlājīfénhuàdǐzhāyǔshuǐxǐtǔzīyuánhuàyúkòngzhìxìngdīqiángdùcáiliào AT gāozhènchāng shuǐxǐlājīfénhuàdǐzhāyǔshuǐxǐtǔzīyuánhuàyúkòngzhìxìngdīqiángdùcáiliào |
_version_ |
1719123057738514432 |