Synthesis and Characterization of a Polymer Containing Electron-Transport Oxadiazole Groups
碩士 === 國立成功大學 === 化學工程學系 === 103 === In this work, we synthesized a polymer (P1) containing oxadiazole groups to be an electron-transport material. P1 was synthesized successfully by Suzuki coupling reaction, and chemical structure of P1 was characterized by 1H-NMR and element analysis. Also, the ph...
Main Authors: | , |
---|---|
Other Authors: | |
Format: | Others |
Language: | zh-TW |
Published: |
2015
|
Online Access: | http://ndltd.ncl.edu.tw/handle/93908327698807659433 |
id |
ndltd-TW-103NCKU5063077 |
---|---|
record_format |
oai_dc |
spelling |
ndltd-TW-103NCKU50630772016-08-15T04:17:43Z http://ndltd.ncl.edu.tw/handle/93908327698807659433 Synthesis and Characterization of a Polymer Containing Electron-Transport Oxadiazole Groups 主鏈含噁二唑衍生物高分子電子傳輸材料的合成與鑑定 Ching-HisangChang 張景翔 碩士 國立成功大學 化學工程學系 103 In this work, we synthesized a polymer (P1) containing oxadiazole groups to be an electron-transport material. P1 was synthesized successfully by Suzuki coupling reaction, and chemical structure of P1 was characterized by 1H-NMR and element analysis. Also, the physical properties (thermal, optical, electrochemical) were investigated from DSC, TGA, optical spectra and cyclic voltammetry respectively. The decomposition temperature (Td) and glass transition temperature (Tg) of P1 are 305.5 oC and 96.2 oC respectively which reveal P1 good thermal stability. In film state, the absorption and photo luminescence peaks of P1 are at 323/383 nm and 442 nm respectively. The HOMO and LUMO levels of P1 are -5.64 eV and -2.73 eV respectively. The LUMO level of P1 (-2.73 eV) is closed to emitting layer HY-PPV (-2.8 eV), meaning P1 should efficiently help electron transporting. The HOMO level of P1 (-5.64 eV) is much lower than HY-PPV (-5.0 eV), meaning P1 exhibits good hole-blocking ability. Yun Chen 陳雲 2015 學位論文 ; thesis 71 zh-TW |
collection |
NDLTD |
language |
zh-TW |
format |
Others
|
sources |
NDLTD |
description |
碩士 === 國立成功大學 === 化學工程學系 === 103 === In this work, we synthesized a polymer (P1) containing oxadiazole groups to be an electron-transport material. P1 was synthesized successfully by Suzuki coupling reaction, and chemical structure of P1 was characterized by 1H-NMR and element analysis. Also, the physical properties (thermal, optical, electrochemical) were investigated from DSC, TGA, optical spectra and cyclic voltammetry respectively. The decomposition temperature (Td) and glass transition temperature (Tg) of P1 are 305.5 oC and 96.2 oC respectively which reveal P1 good thermal stability. In film state, the absorption and photo luminescence peaks of P1 are at 323/383 nm and 442 nm respectively. The HOMO and LUMO levels of P1 are -5.64 eV and -2.73 eV respectively. The LUMO level of P1 (-2.73 eV) is closed to emitting layer HY-PPV (-2.8 eV), meaning P1 should efficiently help electron transporting. The HOMO level of P1 (-5.64 eV) is much lower than HY-PPV (-5.0 eV), meaning P1 exhibits good hole-blocking ability.
|
author2 |
Yun Chen |
author_facet |
Yun Chen Ching-HisangChang 張景翔 |
author |
Ching-HisangChang 張景翔 |
spellingShingle |
Ching-HisangChang 張景翔 Synthesis and Characterization of a Polymer Containing Electron-Transport Oxadiazole Groups |
author_sort |
Ching-HisangChang |
title |
Synthesis and Characterization of a Polymer Containing Electron-Transport Oxadiazole Groups |
title_short |
Synthesis and Characterization of a Polymer Containing Electron-Transport Oxadiazole Groups |
title_full |
Synthesis and Characterization of a Polymer Containing Electron-Transport Oxadiazole Groups |
title_fullStr |
Synthesis and Characterization of a Polymer Containing Electron-Transport Oxadiazole Groups |
title_full_unstemmed |
Synthesis and Characterization of a Polymer Containing Electron-Transport Oxadiazole Groups |
title_sort |
synthesis and characterization of a polymer containing electron-transport oxadiazole groups |
publishDate |
2015 |
url |
http://ndltd.ncl.edu.tw/handle/93908327698807659433 |
work_keys_str_mv |
AT chinghisangchang synthesisandcharacterizationofapolymercontainingelectrontransportoxadiazolegroups AT zhāngjǐngxiáng synthesisandcharacterizationofapolymercontainingelectrontransportoxadiazolegroups AT chinghisangchang zhǔliànháněèrzuòyǎnshēngwùgāofēnzidiànzichuánshūcáiliàodehéchéngyǔjiàndìng AT zhāngjǐngxiáng zhǔliànháněèrzuòyǎnshēngwùgāofēnzidiànzichuánshūcáiliàodehéchéngyǔjiàndìng |
_version_ |
1718375684446879744 |