The Characterization of MixedLithium-Based Oxide for electrodes
碩士 === 國立臺灣海洋大學 === 電機工程學系 === 106 === The purpose of this thesis is to investigate the electrode characteristics of lithium-based oxides. The experiment uses a Sol-gel method, Using precursor metal salt Zn(CH₃COO)₂ mixed precursor metal salt LiCl. Preparation of film by spin coating. Metal film for...
| Main Authors: | , |
|---|---|
| Other Authors: | |
| Format: | Others |
| Language: | zh-TW |
| Published: |
2018
|
| Online Access: | http://ndltd.ncl.edu.tw/handle/2s94h5 |
| Summary: | 碩士 === 國立臺灣海洋大學 === 電機工程學系 === 106 === The purpose of this thesis is to investigate the electrode characteristics of lithium-based oxides. The experiment uses a Sol-gel method, Using precursor metal salt Zn(CH₃COO)₂ mixed precursor metal salt LiCl. Preparation of film by spin coating. Metal film formed by high temperature annealing atmosphere under vacuum. X-ray diffraction (XRD) was used to observe the physical properties to obtain annealing temperature parameters. And mixing the precursor metal salt zinc acetate and lithium chloride in the same ratio. Prepared into a positive electrode powder material after high temperature annealing. And the battery is made by pressing the button battery.
|
|---|