Open-framework Structures Built by Inorganic Clusters : Synthesis and Characterization

• Main Author: Chen, Hong
• Format: Doctoral Thesis
• Language: English
• Published: Stockholms universitet, Institutionen för material- och miljökemi (MMK) 2014
• Subjects: Open-framework; germanates; vanadoborates; aluminoborates; germanosilicates; crystal structure; hydrothermal synthesis; crystal X-ray diffraction; rotation electron diffraction; powder X-ray diffraction
• Online Access: http://urn.kb.se/resolve?urn=urn:nbn:se:su:diva-106853; http://nbn-resolving.de/urn:isbn:978-91-7447-962-1

Novel open-framework germanates and vanadoborates, which are constructed from typical types of clusters, have been synthesized based on different strategies. The crystal structures are solved by using single crystal X-ray diffraction (SXRD) technique or by combined techniques. Additionally, the structures of two open-framework materials, PKU-3 and PKU-16, are determined from nano-sized crystals by rotation electron diffraction (RED) combined with powder X-ray diffraction (PXRD). This thesis serves as an introduction to synthesis of open-framework germanates and vanadoborates based on different design strategies. Two germanates are obtained; SU-74 is achieved by employing a novel structure directing agent (SDA), SUT-8 is achieved by assembling the novel structure building units (SBUs) of Co@Ge14 with the introduction of cobalt ions in the synthesis. Four strategies are successfully used in construction of open-framework vanadoborates: using metal-oxo polyhedra as the linkages in SUT-6; applying the scale chemistry approach in SUT-7; employing metal-organic complexes as the linkages in SUT-12, SUT-13, SUT-14; and introducing covalent bond organic linkages into SUT-10 and SUT-11. Single crystal X-ray diffraction is used to conduct the structure determination in combination with other techniques. Furthermore, the structures of two open-framework materials, an aluminoborate PKU-3 and a germanosilicate PKU-16, are solved from nano-sized crystals using RED data. The structures are further confirmed by Rietveld refinement against PXRD data. The advantages of the RED techniques are demonstrated in two aspects. In PKU-3, the presence of seriously preferred orientation and light elements in the structure makes it difficult for structure determination by PXRD, but it is easier by RED. In PKU-16, the RED technique is used to determine its structure from the as-synthesized multi-phasic sample containing nano-sized crystals. After the structure of PKU-16 has been solved, the synthesis of this interesting phase can be optimized and pure PKU-16 can be obtained. Keywords: Open-framework, germanates, vanadoborates, aluminoborates, germanosilicates, crystal structure, hydrothermal synthesis, single crystal X-ray diffraction, rotation electron diffraction, powder X-ray diffraction