Atomistic Studies of Point Defect Migration Rates in the Iron-Chromium System
Generation and migration of helium and other point defects under irradiation causes ferritic steels based on the Fe-Cr system to age and fail. This is motivation to study point defect migration and the He equation of state using atomistic simulations due to the steels' use in future reactors. A...
Main Author: | Hetherly, Jeffery |
---|---|
Other Authors: | Srivilliputhur, Srinivasan Gopalan |
Format: | Others |
Language: | English |
Published: |
University of North Texas
2010
|
Subjects: | |
Online Access: | https://digital.library.unt.edu/ark:/67531/metadc30463/ |
Similar Items
-
Cascade fragmentation: deviation from power law in primary radiation damage
by: A. E. Sand, et al.
Published: (2017-09-01) -
Effects of Carbon on Fracture Mechanisms in Nanocrystalline BCC Iron - Atomistic Simulations
by: Hyde, Brian
Published: (2014) -
Atomistic studies of defects in bcc iron: dislocations and gas bubbles
by: Hayward, Erin G.
Published: (2012) -
Defects and Calcium Diffusion in Wollastonite
by: Sumudu Nimasha, et al.
Published: (2020-11-01) -
BCC metals in extreme environments : modelling the structure and evolution of defects
by: Gilbert, Mark R.
Published: (2010)