Biodegradation properties of poly (lactic) acid reinforced by kenaf fibers
This study was conducted to study the degradation of poly (lactic acid) and its composites under natural landfill burial. Composites reinforced with natural fibres were expected to degrade faster than polymer itself. PLA was compounded with kenaf bast fibre (KBC) and kenaf core fibre (KCC) with twin...
Main Authors: | , , , |
---|---|
Format: | Article |
Language: | English |
Published: |
Polish Academy of Sciences
2016
|
Subjects: | |
Online Access: | View Fulltext in Publisher View in Scopus |
LEADER | 02454nam a2200373Ia 4500 | ||
---|---|---|---|
001 | 10.12693-APhysPolA.129.835 | ||
008 | 220120s2016 CNT 000 0 und d | ||
020 | |a 05874246 (ISSN) | ||
245 | 1 | 0 | |a Biodegradation properties of poly (lactic) acid reinforced by kenaf fibers |
260 | 0 | |b Polish Academy of Sciences |c 2016 | |
520 | 3 | |a This study was conducted to study the degradation of poly (lactic acid) and its composites under natural landfill burial. Composites reinforced with natural fibres were expected to degrade faster than polymer itself. PLA was compounded with kenaf bast fibre (KBC) and kenaf core fibre (KCC) with twin screw extrusion at temperature range 150-160 °C and being compression moulded at 170 °C for 8 minutes. Samples were then cut prior to testing by burying under composting area in UiTM Shah Alam, Selangor, Malaysia for 6 month period. Samples were measured and observed monthly for the degradation of composites by weight loss and microscopic observation. As expected weight loss for kenaf bast composite (KBC) and kenaf core composite (KCC) was found to be higher, 15.9% and 17.1% respectively, than that of pure PLA of only 4.14%. Microscopic observation confirms degradation has occurred on surface of composites by making cracks, holes, and black spots on all samples, however degradation was more obvious on composites. FTIR analysis shows that spectra of exposed composites were reduced compared to those of unexposed composites. | |
650 | 0 | 4 | |a Biodegradation |
650 | 0 | 4 | |a Extrusion |
650 | 0 | 4 | |a Fibers |
650 | 0 | 4 | |a Fourier transform infrared spectroscopy |
650 | 0 | 4 | |a FTIR analysis |
650 | 0 | 4 | |a Hemp |
650 | 0 | 4 | |a Kenaf bast fibres |
650 | 0 | 4 | |a Kenaf core fibres |
650 | 0 | 4 | |a Kenaf fibers |
650 | 0 | 4 | |a Microscopic observations |
650 | 0 | 4 | |a Poly lactic acid |
650 | 0 | 4 | |a Reinforced plastics |
650 | 0 | 4 | |a Reinforcement |
650 | 0 | 4 | |a Temperature range |
650 | 0 | 4 | |a Twin screw extrusion |
650 | 0 | 4 | |a Weight loss |
700 | 1 | 0 | |a Azmi, N.N. |e author |
700 | 1 | 0 | |a Hassan, N.A. |e author |
700 | 1 | 0 | |a Jaafar, W.N.R.W. |e author |
700 | 1 | 0 | |a Surip, S.N. |e author |
773 | |t Acta Physica Polonica A |x 05874246 (ISSN) |g 129 4, 835-837 | ||
856 | |z View Fulltext in Publisher |u https://doi.org/10.12693/APhysPolA.129.835 | ||
856 | |z View in Scopus |u https://www.scopus.com/inward/record.uri?eid=2-s2.0-84971373666&doi=10.12693%2fAPhysPolA.129.835&partnerID=40&md5=67382746934dc564fd54a5eb91994d6c |