Intercalations and characterization of zinc/aluminium layered double hydroxide-cinnamic acid
Cinnamic acid (CA) is known to lose its definite function by forming into radicals that able to penetrate into the skin and lead to health issues. Incorporating CA into zinc/aluminum-layered double hydroxides (Zn/Al-LDH) able to reduce photodegradation and eliminate close contact between skin and CA...
Main Authors: | , , , , |
---|---|
Format: | Article |
Language: | English |
Published: |
Diponegoro University
2019
|
Subjects: | |
Online Access: | View Fulltext in Publisher View in Scopus |
LEADER | 03214nam a2200361Ia 4500 | ||
---|---|---|---|
001 | 10.9767-bcrec.14.1.3328.165-172 | ||
008 | 220121s2019 CNT 000 0 und d | ||
020 | |a 19782993 (ISSN) | ||
245 | 1 | 0 | |a Intercalations and characterization of zinc/aluminium layered double hydroxide-cinnamic acid |
260 | 0 | |b Diponegoro University |c 2019 | |
650 | 0 | 4 | |a Aluminum compounds |
650 | 0 | 4 | |a Controlled release |
650 | 0 | 4 | |a Field emission scanning electron microscopes |
650 | 0 | 4 | |a Fourier transform infrared attenuated total reflectances |
650 | 0 | 4 | |a Fourier transform infrared spectroscopy |
650 | 0 | 4 | |a Intercalated compounds |
650 | 0 | 4 | |a Interlayer regions |
650 | 0 | 4 | |a Layered double hydroxides |
650 | 0 | 4 | |a Layered Structures |
650 | 0 | 4 | |a Nanocomposites |
650 | 0 | 4 | |a Nitrates |
650 | 0 | 4 | |a Powder X-ray diffraction (pXRD) |
650 | 0 | 4 | |a Scanning electron microscopy |
650 | 0 | 4 | |a Zinc compounds |
856 | |z View Fulltext in Publisher |u https://doi.org/10.9767/bcrec.14.1.3328.165-172 | ||
856 | |z View in Scopus |u https://www.scopus.com/inward/record.uri?eid=2-s2.0-85060737326&doi=10.9767%2fbcrec.14.1.3328.165-172&partnerID=40&md5=3b5017ddbc64bd84d4b8d0e80e19d9fd | ||
520 | 3 | |a Cinnamic acid (CA) is known to lose its definite function by forming into radicals that able to penetrate into the skin and lead to health issues. Incorporating CA into zinc/aluminum-layered double hydroxides (Zn/Al-LDH) able to reduce photodegradation and eliminate close contact between skin and CA. Co-precipitation or direct method used by using zinc nitrate hexahydrate and aluminium nitrate nonahydrate as starting precursors with addition of various concentration of CA. The pH were kept constant at 7±0.5. Fourier Transform Infrared-Attenuated Total Reflectance (FTIR-ATR) shows the presence of nanocomposites peak 3381 cm–1 for OH group, 1641 cm–1 for C=O group, 1543 cm–1 for C=C group and 1206 cm–1 for C–O group and disappearance of N–O peak at 1352 cm–1 indicates that cinnamic acid were intercalated in between the layered structures. Powder X-Ray Diffraction (PXRD) analysis for Zn/Al-LDH show the basal spacing of 9.0 Ǻ indicates the presence of nitrate and increases to 18.0 Ǻ in basal spacing in 0.4M Zn/Al-LDH-CA. CHNS analysis stated that 40 % of cinnamic acid were being found and intercalated in between the interlayer region of the Zn/Al-LDH with higher thermal stability. Field Emission Scanning Electron Microscope (FESEM) images of 0.4 M Zn/Al-LDH-CA shows that the nanocomposites are in more compact, flaky non porous, large agglomerates with smooth the surfaces of the intercalated compound. Controlled release was successful with 80 % release in phosphite anion and 70 % release carbonate anion. The cinnamic acid was successfully inserted between the interlayer regions of Zn/Al-LDH with slow release formulation. Copyright © 2019 BCREC Group. All rights reserved. | |
700 | 1 | 0 | |a Adam, N. |e author |
700 | 1 | 0 | |a Dzulkifli, N.N. |e author |
700 | 1 | 0 | |a Hak, C.R.C. |e author |
700 | 1 | 0 | |a Mohd Ghazali, S.A.I.S. |e author |
700 | 1 | 0 | |a Sarijo, S.H. |e author |
773 | |t Bulletin of Chemical Reaction Engineering & Catalysis |x 19782993 (ISSN) |g 14 1, 165-172 |