Towards high-index-glass based monomode holey fibre with large-mode-area
A high-index (n=1.80) glass based holey fibre was fabricated. The conventional capillary-stacking technique was used to make this fibre characterized by a complicated microstructured cladding. Monomode guidance was observed at 800nm in this fibre and the effective mode area Aeff was measured as ~40µ...
| Main Authors: | , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
2004-02-05.
|
| Subjects: | |
| Online Access: | Get fulltext |
| Summary: | A high-index (n=1.80) glass based holey fibre was fabricated. The conventional capillary-stacking technique was used to make this fibre characterized by a complicated microstructured cladding. Monomode guidance was observed at 800nm in this fibre and the effective mode area Aeff was measured as ~40µm<sup>2</sup>. |
|---|