On the early stage isothermal oxidation of APS CoNiCrAlY coatings

The aim of this study is to analyze the evolution of microstructural and room temperature mechanical properties of air plasma sprayed (APS) CoNiCrAlY coatings before and after early stage high-temperature oxidation. To this purpose, selected samples were isothermally heat treated at 1110 °C for diff...

Full description

Bibliographic Details
Main Authors: Di Girolamo, G. (Author), Alfano, M. (Author), Pagnotta, L. (Author), Taurino, A. (Author), Zekonyte, J. (Author), Wood, R.J.K (Author)
Format: Article
Language:English
Published: 2012-09.
Subjects:
Online Access:Get fulltext
LEADER 01552 am a22001813u 4500
001 352171
042 |a dc 
100 1 0 |a Di Girolamo, G.  |e author 
700 1 0 |a Alfano, M.  |e author 
700 1 0 |a Pagnotta, L.  |e author 
700 1 0 |a Taurino, A.  |e author 
700 1 0 |a Zekonyte, J.  |e author 
700 1 0 |a Wood, R.J.K.  |e author 
245 0 0 |a On the early stage isothermal oxidation of APS CoNiCrAlY coatings 
260 |c 2012-09. 
856 |z Get fulltext  |u https://eprints.soton.ac.uk/352171/1/10.1007_s11665-011-0115-x%255B1%255D.pdf 
520 |a The aim of this study is to analyze the evolution of microstructural and room temperature mechanical properties of air plasma sprayed (APS) CoNiCrAlY coatings before and after early stage high-temperature oxidation. To this purpose, selected samples were isothermally heat treated at 1110 °C for different durations. Phase analysis and oxide scale characterization were performed using x-ray diffraction. Morphological and microstructural features of as-sprayed and oxidized CoNiCrAlY coatings were analyzed by scanning electron microscopy and energy dispersive x-ray spectroscopy. After heat treatment, a duplex oxide scale, composed of an inner ?-Al2O3 layer and an outer spinel-type oxide layer, was observed on coating top-surface. The nanoindentation technique was employed to study the evolution of the mechanical properties. An increase in Young's modulus and hardness with increasing the aging time was observed, this effect was mainly addressed to the partial densification of coating microstructure. 
655 7 |a Article