A Novel γ′-Strengthened Nickel-Based Superalloy for Laser Powder Bed Fusion
An experimental printable γ′‑strengthened nickel-based superalloy, MAD542, is proposed. By process optimization, a crack‑free component with less than 0.06% defect was achieved by laser powder bed fusion (LPBF). After post‑processing by solution heat treatment, a recrystallized structure was reveale...