High-Temperature Corrosion of AlCrSiN Film in Ar-1%SO2 Gas
AlCrSiN film with a composition of 29.1Al-17.1Cr-2.1Si-51.7N in at. % was deposited on a steel substrate by cathodic arc ion plating at a thickness of 1.8 μm. It consisted of nanocrystalline hcp-AlN and fcc-CrN, where a small amount of Si was dissolved. Corrosion tests were carried out at 800 °C for...