Hot Corrosion Behavior of BaLa<sub>2</sub>Ti<sub>3</sub>O<sub>10</sub> Thermal Barrier Ceramics in V<sub>2</sub>O<sub>5</sub> and Na<sub>2</sub>SO<sub>4</sub> + V<sub>2</sub>O<sub>5</sub> Molten Salts
BaLa<sub>2</sub>Ti<sub>3</sub>O<sub>10</sub> ceramics for thermal barrier coating (TBC) applications were fabricated, and exposed to V<sub>2</sub>O<sub>5</sub> and Na<sub>2</sub>SO<sub>4</sub> + V<sub>2</sub...