Effects of hot isostatic pressing temperature on casting shrinkage densification and microstructure of Ti6Al4V alloy
The Ti6Al4V alloy castings were produced by the investment casting process, and the hot isostatic pressing (HIP) was used to remove shrinkage from castings. The processing pressure and holding time for HIP were 150 MPa and 20 min, respectively. Four different HIP temperatures were tested, including...