Microstructure Evolution and Mechanical Properties of FeCoCrNiCuTi<sub>0.8</sub> High-Entropy Alloy Prepared by Directional Solidification
A CoCrCuFeNiTi<sub>0.8</sub> high-entropy alloy was prepared using directional solidification techniques at different withdrawal rates (50 μm/s, 100 μm/s, 500 μm/s). The results showed that the microstructure was dendritic at all withdrawal rates. As the withdrawal rate increased, the de...