Microstructure evolution during homogenization and hot workability of 7055 aluminum alloy produced by twin-roll casting
7055 aluminum alloy was produced by twin-roll casting (TRC) and by conventional mold casting (MC). Homogenization at 465 °C for 24 h with natural cooling was applied, followed by uniaxial hot compression tests to verify the hot workability of the alloy. The results show that the TRC sample possessed...