Nucleation and evolution of β phase and corresponding intergranular corrosion transition at 100–230 °C in 5083 alloy containing Er and Zr
The intergranular corrosion and β phase evolution of 5083 aluminum alloy containing Er and Zr during annealing at 100–230 °C were studied using mass loss tests and transmission electron microscopy. The mass loss curves showed that when annealing temperature changed from 200 to 220 °C, the alloy was...