Microstructure, Texture, and Strength Development during High-Pressure Torsion of CrMnFeCoNi High-Entropy Alloy

Microstructure, Texture, and Strength Development during High-Pressure Torsion of CrMnFeCoNi High-Entropy Alloy

The equiatomic face-centered cubic high-entropy alloy CrMnFeCoNi was severely deformed at room and liquid nitrogen temperature by high-pressure torsion up to shear strains of about 170. Its microstructure was analyzed by X-ray line profile analysis and transmission electron microscopy and its textur...

Full description

Bibliographic Details
Main Authors: Werner Skrotzki, Aurimas Pukenas, Eva Odor, Bertalan Joni, Tamas Ungar, Bernhard Völker, Anton Hohenwarter, Reinhard Pippan, Easo P. George
Format: Article
Language:English
Published: MDPI AG 2020-04-01
Series:Crystals
Subjects:
high-entropy alloy
high-pressure torsion
microstructure
texture
phase transformation
strength
Online Access:https://www.mdpi.com/2073-4352/10/4/336

Internet

https://www.mdpi.com/2073-4352/10/4/336