Microstructural Characterization and Mechanical Properties of Direct Quenched and Partitioned High-Aluminum and High-Silicon Steels
A new experimental steel containing in weight percent 0.3C-2.0Mn-0.5Si-1.0Al-2.2Cr and 0.3C-1.9Mn-1.0Si-1.0Cr was hot rolled in a laboratory rolling mill and directly quenched within the martensite start and finish temperature range. It was then partitioned without reheating during slow furnace cool...