Characterisation of Mn0.63Zn0.37Fe2O4 powders after intensive milling and subsequent thermal treatment
Commercial Mn-Zn powder (Mn0.63Zn0.37Fe2O4, 93 wt. % and Fe2O3 7 wt. %) was milled 0.5, 1, 2 and 4 hours in a planetary ball mill. The goal was to observe intensive milling influences on oxidation and reduction processes that will happen during subsequent heating. Powders were characterized...