Characterisation of Mn0.63Zn0.37Fe2O4 powders after intensive milling and subsequent thermal treatment
Commercial Mn-Zn powder (Mn0.63Zn0.37Fe2O4, 93 wt. % and Fe2O3 7 wt. %) was milled 0.5, 1, 2 and 4 hours in a planetary ball mill. The goal was to observe intensive milling influences on oxidation and reduction processes that will happen during subsequent heating. Powders were characterized...
Main Authors: | Labus Nebojša, Vasiljević Zorka, Aleksić Obrad, Luković Miloljub, Marković Smilja, Pavlović Vladimir, Mentus Slavko, Nikolić Maria Vesna |
---|---|
Format: | Article |
Language: | English |
Published: |
International Institute for the Science of Sintering, Beograd
2017-01-01
|
Series: | Science of Sintering |
Subjects: | |
Online Access: | http://www.doiserbia.nb.rs/img/doi/0350-820X/2017/0350-820X1704455L.pdf |
Similar Items
-
β-Li0.37Na0.63Fe(MoO4)2
by: Amira Souilem, et al.
Published: (2014-02-01) -
Caracterização elétrica de camadas epitaxiais de In0,71Ga0,29As0,63P0,37
by: Shibli, Suhaila Maluf
Published: (1987) -
Crystal structure at (T = 295 and 173 K) of[(NH4)0.63Li0.37]2TeBr6
by: R. Karray, et al.
Published: (2014-04-01) -
Reheating of zinc-titanate sintered specimens
by: Labus N., et al.
Published: (2015-01-01) -
Hydrothermal synthesis and crystal structure analysis of two new cadmium bismuthates, CdBi2O6 and Cd0.37Bi0.63O1.79
by: N. Kumada, et al.
Published: (2015-09-01)