Effects of TiB<sub>2</sub> Particles on the Microstructure Evolution and Mechanical Properties of B<sub>4</sub>C/TiB<sub>2</sub> Ceramic Composite

B<sub>4</sub>C/TiB<sub>2</sub> ceramic composites reinforced with three size scales (average particle size: 7 μm, 500 nm, and 50 nm) of TiB<sub>2</sub> were prepared by using a pressureless sintering furnace at 2100 °C under Ar atmosphere for 60 min. The results d...