Microstructure homogeneity of milled aluminum A356–Si3N4 metal matrix composite powders
A metal matrix composite was produced by co-milling an A356 aluminum alloy powder obtained by rotating electrode off-equilibrium solidification, with different mass fractions (10, 20 and 30%) of Si3N4. The structural and microstructural modifications occurring during the milling were investigated wi...