Microstructure and mechanical properties of a CuNiTi alloy with a large product of strength and elongation
A Cu-10 Ni-2Ti wt.% alloy has been fabricated by induction melting and casting. The microstructure evolutions of the studied alloy treated with thermal-mechanical treatment were characterized. After homogenized at 950 °C for four hours, hot rolling by 80% at 900 °C solid solution treated at 970 °C f...