Phase stability of single phase Al0.12CrNiFeCo high entropy alloy upon irradiation
Phase stability of NiCoFeCr and Al0.12NiCoFeCr single phase high entropy alloys (HEAs) was studied under 3 MeV Ni2+ irradiation at 500 °C to a fluence of 1 × 1017/cm2 reaching a peak dose of ~100 displacements per atom (dpa). Transmission electron microscopy (TEM) diffraction pattern and scanning tr...