Microstructures and Properties of FGH96/DD6 Joints Brazed at Vacuum Pressure State
Ni-Cr-B brazing filler was used to braze FGH96 and DD6 at 1120℃/10 min and 1120℃/10 min/2 MPa. The tensile strength of the joints was tested, the microstructures and fractures were observed by OM and SEM, and the reaction products were analyzed by EPMA. The results show that the joints brazed at vac...