On the Formation of Micro-Shrinkage Porosities in Ductile Iron Cast Components

On the Formation of Micro-Shrinkage Porosities in Ductile Iron Cast Components

A combination of direct austempering after solidification (DAAS) treatment and electron backscatter diffraction (EBSD) method was used to study the formation of micro-shrinkage porosities in ductile iron. Analyzing the aus-ferritic microstructure revealed that most of micro-shrinkage porosities are...