The Effect of Cooling Rate after Homogenization on the Microstructure and Properties of 2017a Alloy Billets for Extrusion with Solution Heat Treatment on the Press
The influence of cooling rate after homogenization on the 2017A alloy microstructure was analysed. The capability of the θ (Al2Cu) particles, precipitated during various homogenization coolings, for rapid dissolution was estimated. For this purpose, the DSC test was used to determine the effect of t...