Temperature Dependence and Microstructure Effects on Magnetic Properties of FePt(B, Ag, C) Film
A FePt(B, Ag, C) granular film was formed from post-annealed B<sub>4</sub>C(1.0 nm)/FePt(Ag, C) layers at a substrate temperature of 470 °C for 2 min. The 6 nm thick FePt(B, Ag, C) film demonstrates high perpendicular magnetic anisotropy (K<sub>u</sub> = 2.83 × 10<sup>7...