Temperature Dependence and Microstructure Effects on Magnetic Properties of FePt(B, Ag, C) Film
A FePt(B, Ag, C) granular film was formed from post-annealed B<sub>4</sub>C(1.0 nm)/FePt(Ag, C) layers at a substrate temperature of 470 °C for 2 min. The 6 nm thick FePt(B, Ag, C) film demonstrates high perpendicular magnetic anisotropy (K<sub>u</sub> = 2.83 × 10<sup>7...
Main Authors: | Jai-Lin Tsai, Shi-Min Weng, Cheng Dai, Jyun-You Chen, Xue-Chang Lu, Ting-Wei Hsu |
---|---|
Format: | Article |
Language: | English |
Published: |
MDPI AG
2021-02-01
|
Series: | Nanomaterials |
Subjects: | |
Online Access: | https://www.mdpi.com/2079-4991/11/2/419 |
Similar Items
-
Influence of an MgTiTaON Inserted Layer on Magnetic Properties and Microstructure of FePtAgC Films
by: Jai-Lin Tsai, et al.
Published: (2019-04-01) -
Enhanced perpendicular coercivity of ultrathin perpendicularly magnetized Tb–Fe–Co films on silicon substrates using a thin Pt underlayer
by: Bang Do, et al.
Published: (2016-03-01) -
Surface and Microstructure Analysis of CoCrPt Film on RuCoCrX (X = Ti, Re) Intermediate Layers
by: Jai-Lin Tsai, et al.
Published: (2020-04-01) -
Pd Seed Under-layer Effect on Coercive Field of Perpendicularly Magnetized Co/Pd Multilayer Films
by: Budi Purnama
Published: (2010-07-01) -
Magnetic Properties and Microstructure of FePt(BN, Ag, C) Films
by: Jai-Lin Tsai, et al.
Published: (2018-10-01)