Extremely rapid age hardening behavior in solution treated Ti-5Al-2Fe-3Mo
To grasp age hardening and phase transformation behaviors in a β rich α+β type titanium alloy, Ti-5Al-2Fe-3Mo, during aging at 300-500°C after the solution treatment at high α+β temperature. Vickers hardness and microstructure changes during aging were closely investigated using XDR and TEM/EDS. Vic...