Influence of cooling conditions and amount of retained austenite on the fracture of austempered ductile iron

Influence of cooling conditions and amount of retained austenite on the fracture of austempered ductile iron

SEM Analysis of fracture surfaces from tensile test specimens of thick-walled, austempered ductile irons (diameter 160 mm) shows different fracture behavior depending on the austenite retained in the matrix. The results show ductile fractures only in areas containing retained austenite sections. In...