Influence of cooling conditions and amount of retained austenite on the fracture of austempered ductile iron
SEM Analysis of fracture surfaces from tensile test specimens of thick-walled, austempered ductile irons (diameter 160 mm) shows different fracture behavior depending on the austenite retained in the matrix. The results show ductile fractures only in areas containing retained austenite sections. In...
Main Authors: | VYACHESLAV GORYANY, ECKART HOFMANN, PAUL JOSEF MAUK |
---|---|
Format: | Article |
Language: | English |
Published: |
Serbian Chemical Society
2008-01-01
|
Series: | Journal of the Serbian Chemical Society |
Subjects: | |
Online Access: | http://www.shd.org.yu/JSCS/Vol73/No1/JSCS-3692.pdf |
Similar Items
-
Influence of cooling conditions and amount of retained austenite on the fracture of austempered ductile iron
by: Goryany Vyacheslav, et al.
Published: (2008-01-01) -
Microstructure and mechanical properties of CuNiMo austempered ductile iron
by: Erić Olivera, et al.
Published: (2004-01-01) -
Evaluation of Volume Fraction of Austenite in Austempering Process of Austempered Ductile Iron
by: Edward Tyrała, et al.
Published: (2019-08-01) -
Effect of nodule count and austempering heat treatment on segregation behavior of alloying elements in ductile cast iron
by: E. Akbarzadeh Chiniforush, et al.
Published: (2016-05-01) -
Effect of sub-zero cooling on microstructure and mechanical properties of a low alloyed austempered ductile iron
by: M. Ardestani, et al.
Published: (2007-05-01)